The invention provides an anticorrosive coating and its preparation method. The preparation method includes: heating epoxy resin to the first temperature, dropping phosphoric acid, mixing, stationary and cooling to obtain the first component; mixing alkyd resin, ethanol and isopropanol evenly to obtain the second component; mixing the first component and the second component, adding dispersant, mixing evenly, adding organic acid, and again. Mixing, get the mixture; adding filler in the mixture, mixing and dispersing, adding defoamer and leveling agent, get the anti-corrosive coating. By modifying with phosphoric acid and adding organic acid, the present invention not only realizes the rusty brushing function of the paint, but also enhances the anticorrosive performance.
【技术实现步骤摘要】
防腐涂料及其制备方法
本专利技术涉及涂料，更具体地，涉及防腐涂料及其制备方法。
技术介绍
普通的环氧带锈防腐涂料一般采用磷酸盐作转锈、稳锈剂，这样的涂料转锈效果差，往往前期腐蚀速度较快。此外，磷酸主要用于水性带锈涂料中，不适宜用于溶剂性涂料。这是因为磷酸中的水分与溶剂型涂料成膜物质的不相容，另外直接在溶剂型涂料中加入磷酸会使涂层严重起泡，造成涂层的保护作用丧失，因此，现有技术中均不会将磷酸用于防腐涂料中，目前的防腐涂料基本上都是普通的环氧带锈防腐涂料，但是这种防腐涂料的转锈效果差，防腐的期限较短，需要定期且频繁的维护。
技术实现思路
本专利技术提供了一种磷酸改性环氧树脂防腐涂料，不仅不会使涂层严重起泡，而且可以提高树脂的防腐性能，实现涂料的带锈涂刷。此外，还可以在涂料中加入有机酸，与铁形成稳定的络合物，保护内层不被腐蚀，防腐效果较好且不需要频繁的维护。本专利技术提供了一种制备防腐涂料的方法，包括：将环氧树脂加热至第一温度，滴加磷酸，搅拌混合，静置，冷却，得到第一组分；将醇酸树脂、乙醇和异丙醇混合均匀，得到第二组分；将所述第一组分和所述第二组分混合，加入分散剂，搅拌均匀...
【技术保护点】
1.一种制备防腐涂料的方法，其特征在于，包括：将环氧树脂加热至第一温度，滴加磷酸，搅拌混合，静置，冷却，得到第一组分；将醇酸树脂、乙醇和异丙醇混合均匀，得到第二组分；将所述第一组分和所述第二组分混合，加入分散剂，搅拌均匀后加入有机酸，再次混合，得到混合物；在所述混合物中加入填料，搅拌分散，加入消泡剂和流平剂，混合得到所述防腐涂料。
【技术特征摘要】
1.一种制备防腐涂料的方法，其特征在于，包括：将环氧树脂加热至第一温度，滴加磷酸，搅拌混合，静置，冷却，得到第一组分；将醇酸树脂、乙醇和异丙醇混合均匀，得到第二组分；将所述第一组分和所述第二组分混合，加入分散剂，搅拌均匀后加入有机酸，再次混合，得到混合物；在所述混合物中加入填料，搅拌分散，加入消泡剂和流平剂，混合得到所述防腐涂料。2.根据权利要求1所述的方法，其特征在于，所述环氧树脂与所述磷酸的质量比为4-8:1-3。3.根据权利要求1所述的方法，其特征在于，所述第一温度为90-110℃。4.根据权利要求1所述的方法，其特征在于，采用的所述磷酸的浓度为85％-90％。5.根据权利要求1所述的方法，其特征在于，所述环氧树脂包括双酚A型环氧树脂和双酚F...
【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：洛阳尖端技术研究院，洛阳尖端装备技术有限公司，
类型：发明
国别省市：河南,41