A heat transfer powder coating is characterized by the following components: 200 400 copies of polyester resin; 20 50 copies of TGIC; 3 8 copies of leveling agent; 1 3 copies of benzoin; 1 3 copies of brightener; 1 3 copies of wax powder; 0.5 1 copies of promoter; 1 3 copies of pigments. The curing degree and crosslinking density of the polyester resin used in the invention are obviously superior to those of other products under the same conditions. Curing at 200 C for 10 minutes can make the coating fully cured, reduce the phenomenon of paper sticking, oil printing and other damage to the coating surface caused by secondary short curing when the coating is heated during high temperature transfer printing, and the cost is low and the manufacture is simple.
【技术实现步骤摘要】
一种热转印涂料
本专利技术属于粉末涂料
，具体涉及到一种热转印粉末涂料。
技术介绍
近几年来热转印技术在铝型材市场取得突飞猛进的发展。粉末涂料热转印技术是将高精度纸上的转印油墨在固定温度下热升华渗入到涂层内部，使型材印上所需图案效果的一种特殊工艺。热转印粉末涂层不会改变原有涂层的物化性能如硬度、耐磨性、耐冲击性、耐盐雾性、耐老化性等，目前滑雪运动产品的图案印刷主要使用的就是热转印技术，但是现有的热转印粉末涂料主要以聚氨酯体系为主，但使用效果较好，但价格昂贵，成本太高。
技术实现思路
本专利技术是针对目前技术中的不足，提供一种热转印粉末涂料及其制备方法。热转印粉末涂料，其特征在于，其包括按质量份的以下组分：热转印涂料制备方法，其特征在于：将所述聚酯树脂、TGIC、流平剂、安息香、光亮剂、蜡粉、促进剂颜料进行预混合，熔融挤出，冷却破碎，粉碎，固化制得热转印底粉样板，将制得的样板通过热转印烫画机进行热转印，制得热转印样板。优选的，热转印温度为200°，固化时间为8-12分钟。优选的，所述聚酯树脂酸值＞40mgKOH·g－1。本专利技术的有益效果是，本专利技术所采用的聚酯树脂在同等条件下的固化程度和交联密度明显优于其他产品，在200℃条件下固化10min，能使涂层充分固化，减少涂层高温转印时受热产生二次短固化而产生的粘纸、油印等损坏涂层表面的现象，且成本低廉，制作简便。具体实施方式实施例一热转印粉末涂料，其包括按质量份的以下组分：其中聚酯树脂酸值为42mgKOH·g－1。该热转印涂料制备方法，将上述比例的聚酯树脂、TGIC、流平剂、安息香、光亮剂、蜡粉、促进剂颜...
【技术保护点】
1.一种热转印粉末涂料，其特征在于，其包括按质量份的以下组分：
【技术特征摘要】
1.一种热转印粉末涂料，其特征在于，其包括按质量份的以下组分：2.一种热转印涂料制备方法，其特征在于：将所述聚酯树脂、TGIC、流平剂、安息香、光亮剂、蜡粉、促进剂颜料进行预混合，熔融挤出，冷却破碎，粉碎，固化制得热转印底粉样板，将制得的...
【专利技术属性】
技术研发人员：罗茂森，
申请(专利权)人：广州经用体育用品有限公司，
类型：发明
国别省市：广东,44