The invention belongs to the drying technology field of pottery products, and specifically discloses a fast steam drying process for pottery bricks, which includes the following steps: (1) preparing semi-finished products with pottery materials and aggregates as raw materials, the granularity of both pottery materials and aggregates are 80 320 meshes; (2) controlling the moisture content of semi-finished products to be less than 6% and the steam drying temperature to be 50 90 C for semi-finished products by steam drying. This process can greatly shorten the drying time of semi-finished products, and the yield of semi-finished products is more than 80%.
【技术实现步骤摘要】
陶土砖蒸汽快速烘干工艺
本专利技术申请属于陶土制品干燥
，具体公开了一种陶土砖蒸汽快速烘干工艺。
技术介绍
陶土砖主要由原料粉碎、制坯、成型(形成半成品)、干燥和烧制几个步骤制备而成。与传统红砖(粘土砖)相比，陶土砖色泽均匀，耐高温，耐严寒，耐腐蚀，耐磨，抗压，经久耐用，永不褪色，具有浓厚的文化气息和时代感，是广场、庭院、街道、广场等场地理想的硬质地面铺设材料。其中，在制备400mm×400mm×50mm以上的大尺寸高强度陶土砖的难度特别大，清朝以前，只有皇宫才有雄厚的资金实力使用该产品，因为以当时的生产实力，陶土砖从制泥到烧制，再到打磨，需要三年左右的周期。由于相当费时费力，生产出高质量的陶土砖，其成本相当高，所以也称金砖，寓意为一匹砖相当于等重的黄金了。另外，随着现代城市建设、人们生活水平和审美程度的提高，相对于小尺寸陶土砖来讲，大尺寸陶土砖更加美观，所以400mm×400mm×50mm及以上的大尺寸高强度陶土砖，是千百年来中外陶业匠人梦寐以求的产品。直至现在，陶业匠要想在半年内生产出高质量的大尺寸高强度陶土砖都是非常困难的，其原因在于：(1)大尺寸半成...
【技术保护点】
1.陶土砖蒸汽快速烘干工艺，其特征在于，包括以下步骤：(1)以陶土材料和骨料为原料制备半成品，所述陶土材料和骨料的粒度均为80‑320目；(2)对半成品蒸汽烘干，控制半成品的水分在6％以下，蒸汽烘干温度为50‑90℃。
【技术特征摘要】
1.陶土砖蒸汽快速烘干工艺，其特征在于，包括以下步骤：(1)以陶土材料和骨料为原料制备半成品，所述陶土材料和骨料的粒度均为80-320目；(2)对半成品蒸汽烘干，控制半成品的水分在6％以下，蒸汽烘干温度为50-90℃。2.根据权利要求1所述的陶土砖蒸汽快速烘干工艺，其特征在于，所述陶土材料包括重庆陶土、仁寿陶土和桂花镇陶土中的一种、两种或者三种。3.根据权利要求1或2所述的陶土砖蒸汽快速烘干工艺，其特征在于，所述陶土材料的质量占比＜50％。4.根据权利要求1或2所述的陶土砖蒸汽快速烘干工艺，其特征在于，所述骨料包括陶产品废料、工业废渣和烧结...
【专利技术属性】
技术研发人员：梁照林，
申请(专利权)人：成都坭韵陶坊有限公司，
类型：发明
国别省市：四川,51