The invention belongs to the technical field of silver alloys, and specifically discloses a corrosion-resistant silver-zinc alloy with reversible discoloration performance and its discoloration process and application. According to the weight content of 100%, the corrosion-resistant Ag-Zn alloy with reversible discoloration performance contains the following components: zinc 30%-65%; silver 35%-70%; and unavoidable impurity elements. The silver-zinc alloy provided by the invention has good casting and stamping properties, controllable color and good reversibility of discoloration performance, good anti-discoloration and corrosion resistance, so it has great application and industrialization value in silver jewelry industry and industry.
【技术实现步骤摘要】
变色性能可逆的耐腐蚀银锌合金及其变色工艺和应用
本专利技术属于银合金
，具体涉及一种变色性能可逆的耐腐蚀银锌合金及其变色工艺和应用。
技术介绍
银是一种重要的贵金属，自从人类发现银以来，银及银合金的应用已经有数千年的历史。银及银合金通常具有良好的导热、导电性能，同时具有优异的加工性能，此外，反射率极高，并拥有较为稳定的理化性质，因此被广泛应用于电子电器和工艺饰品中。将银及银合金用在珠宝首饰中既有优点也有缺点，表1中总结了各种银及银合金作为珠宝首饰的组成成分、优缺点。从表1可知，通过不同的合金成分的设计及处理工艺，可以使得银及银合金各具特色。但是，容易氧化变黑是这些银及银合金面临的一个共同问题。特别地，这些银饰品在佩戴时与人体汗液、空气中的硫化氢和氧气等接触时，容易被腐蚀氧化，从而产生发黑、色泽不均等问题。为了防止出现这样的问题，目前通过在银饰品表面进行防腐处理，即使用表面镀膜、表面改性等表面处理工艺，使得银饰品具有一定的防腐效果，在一定程度上延缓了银及银合金的氧化发黑问题，并且可以赋予银合金某些特别的外观颜色，比如玫瑰金色。然而实际效果并不理想，首饰佩戴一段...
【技术保护点】
1.一种变色性能可逆的耐腐蚀银锌合金，其特征在于，按照重量含量为100％计，所述银锌合金包含以下组分：锌30％～65％；银35％～70％；以及不可避免的杂质元素。
【技术特征摘要】
1.一种变色性能可逆的耐腐蚀银锌合金，其特征在于，按照重量含量为100％计，所述银锌合金包含以下组分：锌30％～65％；银35％～70％；以及不可避免的杂质元素。2.如权利要求1所述的变色性能可逆的耐腐蚀银锌合金，其特征在于，所述耐腐蚀银锌合金的物相中包含ξ相和β1相中的至少一种。3.如权利要求1所述的变色性能可逆的耐腐蚀银锌合金，其特征在于，所述耐腐蚀银锌合金的表面具有一层氧化膜。4.如权利要求3所述的变色性能可逆的耐腐蚀银锌合金，其特征在于，所述氧化膜为氧化锌膜。5.如权利要求3所述的变色性能可逆的耐腐蚀银锌合金，其特征在于，所述氧化膜的厚度为0～10μm。6.如权利要求1～5任一项所述的变色性能可逆的耐腐蚀银锌合金的变色工艺，其特征在于，将所述耐腐蚀银锌合金置于150℃～280℃的环境中保温，随后退火处理，即可使得所述耐腐蚀银锌合金呈银白色；将所述耐腐蚀银锌合金置于温度...
【专利技术属性】
技术研发人员：江涛，邬治平，钟飞，赵均辉，杨丽，
申请(专利权)人：依波精品深圳有限公司，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。