The invention relates to a paint additive, in particular to a paint additive with good anti-scaling performance, which comprises 20 30 parts of butyraldehyde oxime, 30 40 parts of cyclohexanone oxime, 15 19 parts of linseed oil, 5 10 parts of castor oil and 80 120 parts of solvent by weight. The paint additive of the invention can prevent the oxidation polymerization of the paint to form a film, delay the formation of the cementitious body and resist the crust, and form a complex with the metal part of the drying agent, thereby losing the drying ability of the paint and delaying its crust. The paint additive of the invention has low price, suitable oxidation and good miscibility with various coatings.
【技术实现步骤摘要】
一种涂料助剂
本专利技术涉及一种涂料助剂,特别是一种抗结皮性能好的涂料助剂。
技术介绍
气干型涂料在使用和贮存过程中的结皮,首先表现为溶剂的挥发,然后是表面氧化聚合而胶凝。早期的胶凝体可通过搅拌而恢复成原来的流体状态,随着时间延长、胶凝体逐步变硬,则可经过滤除去。若皮膜足够硬时,可直接切划而捞除。最后,皮膜增厚以致全部凝胶而成固态。形成结皮的原因有三方面:(1)涂料表面与空气接触,二使涂料表面氧化聚合。(2)因溶剂挥发而促使胶化。(3)由于以上两因素而破坏连接料的胶体平衡。在油漆的生产过程中,常使用溶剂覆盖等隔离空气的措施以延迟结皮,但效果不明显。
技术实现思路
本专利技术需要解决的技术问题是提供一种抗结皮性能优良的涂料助剂。为解决上述技术问题,本专利技术的涂料助剂包括丁醛肟20-30份,环乙酮肟30-40份,亚麻油15-19份,蓖麻油5-10份,溶剂80-120份。进一步的,还包括表面活性剂,所述表面活性剂5-8份。更进一步的,所述表面活性剂为硬脂酸钠或脂肪酸甘油酯。更进一步的,所述溶剂为双戊烯。更进一步的,丁醛肟20份,环乙酮肟40份,亚麻油15份,蓖麻油10份,硬脂酸钠5份,双戊烯120份。更进一步的,丁醛肟30份,环乙酮肟30份,亚麻油19份,蓖麻油5份,硬脂酸钠8份,双戊烯80份。更进一步的,丁醛肟26份,环乙酮肟33份,亚麻油16份,蓖麻油7份,脂肪酸甘油酯6份,双戊烯110份。更进一步的,丁醛肟23份,环乙酮肟37份,亚麻油18份,蓖麻油9份,脂肪酸甘油酯7份,双戊烯120份。本专利技术的涂料助剂能够阻止涂料的氧化聚合成膜,能延迟胶凝体的形成而抗 ...
【技术保护点】
1.一种涂料助剂,其特征在于以质量份计包括:丁醛肟20‑30份,环乙酮肟30‑40份,亚麻油15‑19份,蓖麻油5‑10份,溶剂80‑120份。
【技术特征摘要】
1.一种涂料助剂,其特征在于以质量份计包括:丁醛肟20-30份,环乙酮肟30-40份,亚麻油15-19份,蓖麻油5-10份,溶剂80-120份。2.按照权利要求1所述的涂料助剂,其特征在于:还包括表面活性剂,所述表面活性剂5-8份。3.按照权利要求2所述的涂料助剂,其特征在于:所述表面活性剂为硬脂酸钠或脂肪酸甘油酯。4.按照权利要求3所述的涂料助剂,其特征在于:所述溶剂为双戊烯。5.按照权利要求4所述的涂料助剂,其特征在于:丁醛肟20份,环乙酮肟40份,...
【专利技术属性】
技术研发人员:杨小康,
申请(专利权)人:丹阳市博元安全生产服务有限公司,
类型:发明
国别省市:江苏,32