The invention relates to a modified polyethylene composite material, in particular to a sprayable polyethylene composite material with high adhesion. The raw material formula is as follows: polyethylene 60 80%, polypropylene 12 25%, compatibilizer 5 15%, antioxidant 0.12 0.6% and ultraviolet resistance 0.2 0.6%, which are obtained by mixing, melt blending, extrusion granulation and grinding powder. Sprayable polyethylene composites. The preparation method of the material is also provided. The polyethylene conforming material prepared by the invention can improve the adhesion of the paint on the products, and has long-term effect, and the effective time can be up to 5 years.
【技术实现步骤摘要】
一种高附着的可喷涂聚乙烯复合材料及其制备方法
本专利技术涉及一种改性聚乙烯复合材料，特别涉及具有高附着可喷涂功能的、适合滚塑生产工艺的聚乙烯材料及其制备方法。
技术介绍
聚乙烯(polyethylene，简称PE)是乙烯经聚合制得的一种热塑性树脂。在工业上，也包括乙烯与少量α-烯烃的共聚物。聚乙烯无臭，无毒，手感似蜡，具有优良的耐低温性能(最低使用温度可达-100～-70℃)，化学稳定性好，能耐大多数酸碱的侵蚀(不耐具有氧化性质的酸)。常温下不溶于一般溶剂，吸水性小，电绝缘性优良。聚乙烯对于环境应力(化学与机械作用)是很敏感的，耐热老化性差于聚合物的化学结构和加工条。聚乙烯可用一般热塑性塑料的成型方法(见塑料加工)加工。用途十分广泛，主要用来制造薄膜、包装材料、容器、管道、单丝、电线电缆、日用品等，并可作为电视、雷达等的高频绝缘材料。随着石油化工的发展，聚乙烯生产得到迅速发展，产量约占塑料总产量的1/4。1983年世界聚乙烯总生产能力为24.65Mt，在建装置能力为3.16Mt。2011年最新统计结果，全球产能达到96Mt，聚乙烯生产的发展趋势显示，生产消费逐步向...
【技术保护点】
1.一种高附着的可喷涂聚乙烯复合材料，其特征在于，所述聚乙烯复合材料的由以下百分比的原料制得：聚乙烯60‑80％、聚丙烯12‑25％、相容剂5‑15％、抗氧剂0.12‑0.6％与抗紫外线剂0.2‑0.6％。
【技术特征摘要】
1.一种高附着的可喷涂聚乙烯复合材料，其特征在于，所述聚乙烯复合材料的由以下百分比的原料制得：聚乙烯60-80％、聚丙烯12-25％、相容剂5-15％、抗氧剂0.12-0.6％与抗紫外线剂0.2-0.6％。2.根据权利要求1所述的一种高附着的可喷涂聚乙烯复合材料，其特征在于，所述的聚乙烯满足：密度为0.910-0.965g/cm3，熔体流动速率为1.0-20.0g/10min。3.根据权利要求1所述的一种高附着的可喷涂聚乙烯复合材料，其特征在于，所述的聚丙烯满足：密度为0.910-0.965g/cm3，熔体流动速率为1.0-20.0g/10min。4.根据权利要求1所述的一种高附着的可喷涂聚乙烯复合材料，其特征在于，所述的相容剂满足：密度为0.850-0.900g/cm3，熔体流动速率为0.5-20.0g/1...
【专利技术属性】
技术研发人员：唐宇航，陈叶茹，温原，
申请(专利权)人：浙江瑞堂塑料科技股份有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。