The invention discloses a preparation method of crosslinked polyethylene insulating material with low temperature conductivity, which includes the following steps: firstly, drying low density polyethylene for 48 hours to ensure that LDPE is clean and dry; secondly, drying low density polyethylene and antioxidant, crosslinking agent and 4,4'-dimethylaminobenzoyl are added into the triple-neck bottle according to the mass ratio of 100:0.1:2:0.3, and xylene is added. Solvent was stirred in oil bath at 110 C for 3 hours to remove xylene and LDPE mixture was obtained. Finally, the sample was pressed and dried in vacuum for 48 hours, so that the impurities produced during the cross-linking process were eliminated. The temperature conductivity of XLPE is significantly improved, which is of great significance for XLPE used in HVDC cables.
【技术实现步骤摘要】
一种低温度电导系数的交联聚乙烯绝缘材料的制备方法
本专利技术涉及高压直流电缆用交联聚乙烯绝缘材料的制备方法，具体涉及一种低温度电导系数的交联聚乙烯绝缘材料的制备方法。
技术介绍
随着高压特高压直流输电技术的发展，高压直流电缆在电力系统中的应用越来越广泛。交联聚乙烯材料由于其优异的机械性能和绝缘性能等优势，作为高压直流电缆绝缘材料被广泛使用。但是在高压直流电缆运行过程中，由于导体发热导致电缆绝缘层内温度由内向外呈梯度分布，绝缘层内部温度较高，绝缘层外部温度较低。在直流条件下，电缆绝缘层内电场分布与绝缘电导有关，而绝缘材料电导又受到温度和电场的影响。在电缆运行过程中，电缆绝缘层内的电场分布会由于绝缘材料随温度产生的变化而产生畸变，严重时会导致电缆绝缘故障的发生。因此，研究能够较低温度电导系数的交联聚乙烯绝缘材料的制备方法具有重要意义。已有研究表明，纳米复合材料能够在一定程度上改善聚乙烯绝缘材料的温度电导特性。然而，由于纳米颗粒在交联聚乙烯绝缘内的分散性难以保证，导致纳米复合绝缘材料很难实现工业化应用。本专利技术基于电压稳定剂填料与交联聚乙烯材料的良好的相容性，提出利用...
【技术保护点】
1.一种低温度电导系数的交联聚乙烯绝缘材料的制备方法，其特征在于，包括如下步骤:(1)将低密度聚乙烯(LDPE)置于干燥箱中，设置温度80℃，干燥48小时，保证LDPE清洁干燥；(2)将干燥的低密度聚乙烯与抗氧剂、交联剂和4,4’—双二甲氨基苯偶酰按照100：0.1：2：0.3的质量比加入三颈瓶中，加入二甲苯溶剂，并在110℃油浴中搅拌3h，得到LDPE混合液；将混合液倒入玻璃模具中，在温度为70℃的烘箱中烘干，以去除二甲苯，得到LDPE混合物；(3)试样压制：先取适量LDPE混合物置于平板硫化机容器槽中，温度设置120℃，加热10min，以使LDPE混合物初步融化；将平板...
【技术特征摘要】
1.一种低温度电导系数的交联聚乙烯绝缘材料的制备方法，其特征在于，包括如下步骤:(1)将低密度聚乙烯(LDPE)置于干燥箱中，设置温度80℃，干燥48小时，保证LDPE清洁干燥；(2)将干燥的低密度聚乙烯与抗氧剂、交联剂和4,4’—双二甲氨基苯偶酰按照100：0.1：2：0.3的质量比加入三颈瓶中，加入二甲苯溶剂，并在110℃油浴中搅拌3h，得到LDPE混合液；将混合液倒入玻璃模具中，在温度为70℃的烘箱中烘干，以去除二甲苯，得到LDPE混合物；(3)试样压制...
【专利技术属性】
技术研发人员：杜伯学，韩晨磊，侯兆豪，李进，张庆超，姜惠兰，
申请(专利权)人：天津大学，
类型：发明
国别省市：天津,12