The invention discloses a steel plate for methanol synthesis tower and its production method. The chemical composition and mass percentage content of the steel plate are C:0.12_0.15%, Si:0.1_0.3%, Mn:0.4_0.6%, P<0.07%, S<0.04%, Cr:2.2_2.5%, Mo:1.0_1.1%, Al:0.2_0.4%, V:0.15_0.25%, and the other impurities are unavoidable. Casting, rolling and heat treatment processes. The steel plate for methanol synthesis tower produced by the invention has uniform structure and meets the requirements of ASME. The tensile strength of the steel plate is 540 670 MPa, the yield strength is more than 330 MPa, the impact strength of the steel plate at 29 C is more than 150J, and the tensile yield strength at 330 C is more than 280 MPa.
【技术实现步骤摘要】
一种甲醇合成塔用钢板及其生产方法
本专利技术属于冶金
，具体涉及一种甲醇合成塔用钢板及其生产方法。
技术介绍
随着煤化工项目装置的大型化，甲醇合成塔装置规模不断扩大，大型甲醇合成塔是甲醇合成装置核心设备，该设备性能将直接影响甲醇合成过程的效率、能耗，同时也将影响到甲醇合成装置的长期运行。甲醇合成塔长期应用于高温、高压的工作环境中，要求设备用钢具有更好的高温性能，即高温下仍能有足够的强度和韧塑性；甲醇合成反应温度处于第一类回火脆化温度范围内，因此钢板应具有足够的抗回火脆化性能；甲醇合成反应处于酸性环境中，因此钢板应具有一定抗酸腐蚀性能；甲醇合成设备较大，通常都是由钢板焊接而成，因此钢板应具有良好的焊接性能。而普通的SA387Gr22CL2钢板通常无法满足以上钢板的使用要求，因此为保证设备正常运行，开发高性能的甲醇合成塔用SA387Gr22Cl2钢板尤为重要。
技术实现思路
本专利技术要解决的技术问题是提供一种甲醇合成塔用钢板及其生产方法。为解决上述技术问题，本专利技术所采取的技术方案是：一种甲醇合成塔用钢板，所述钢板化学成分组成及其质量百分含量为：C：0.12-0...
【技术保护点】
1.一种甲醇合成塔用钢板，其特征在于，所述钢板化学成分组成及其质量百分含量为：C：0.12‑0.15%，Si：0.1‑0.3%，Mn：0.4‑0.6%，P≤0.07%，S≤0.04%，Cr：2.2‑2.5%，Mo：1.0‑1.1%，Al：0.2‑0.4%，V：0.15‑0.25%，其余为Fe和不可避免杂质。
【技术特征摘要】
1.一种甲醇合成塔用钢板，其特征在于，所述钢板化学成分组成及其质量百分含量为：C：0.12-0.15%，Si：0.1-0.3%，Mn：0.4-0.6%，P≤0.07%，S≤0.04%，Cr：2.2-2.5%，Mo：1.0-1.1%，Al：0.2-0.4%，V：0.15-0.25%，其余为Fe和不可避免杂质。2.根据权利要求1所述的一种甲醇合成塔用钢板，其特征在于，所述钢板厚度为100-125mm，钢板探伤满足NB/T47013.3I级。3.根据权利要求1所述的一种甲醇合成塔用钢板，其特征在于，所述钢板抗拉强度540-670MPa，屈服强度≥330MPa，钢板-29℃冲击均≥150J，330℃高温拉伸屈服强度≥280MPa。4.基于权利要求1-3任意一项所述的一种甲醇合成塔用钢板的生产方法，其特征在于，所述生产方法包括冶炼、浇铸、轧制及热处理工序；所述冶炼工序，在电炉中炼钢，在精炼炉中...
【专利技术属性】
技术研发人员：邓建军，李杰，龙杰，侯敬超，袁锦程，吴艳阳，牛红星，尹卫江，李样兵，顾自有，王东阳，金武涛，
申请(专利权)人：舞阳钢铁有限责任公司，
类型：发明
国别省市：河南,41