一种辐照交联聚乙烯泡棉材料及其制备方法技术

本发明专利技术涉及一种辐照交联聚乙烯泡棉材料及其制备方法，具体地，本发明专利技术制备方法在低密度聚乙烯、发泡剂、敏化剂和抗氧化剂中加入碳九石油树脂作为增强剂，通过调整碳九石油树脂种类和用量，制得高刚性聚乙烯泡棉材料。本发明专利技术所述的方法只制得的产品刚性高，弹性模量在5MPa以上，在地垫、汽车内饰、电子设备等领域具有广泛应用。

A kind of irradiated crosslinked polyethylene foam material and its preparation method

The invention relates to an irradiated cross-linked polyethylene foam material and a preparation method. Specifically, the preparation method of the invention adds C9 petroleum resin as reinforcing agent in low density polyethylene, foaming agent, sensitizer and antioxidant, and by adjusting the type and amount of C9 petroleum resin, a high rigidity polyethylene foam material is prepared. The method of the invention only produces products with high rigidity and modulus of elasticity over 5 MPa, and has wide application in the fields of mattress, automobile interior decoration, electronic equipment, etc.

【技术实现步骤摘要】
一种辐照交联聚乙烯泡棉材料及其制备方法
本专利技术属于高分子材料
，具体涉及一种辐照交联聚乙烯泡棉材料及其制备方法。
技术介绍
辐射交联聚乙烯泡沫塑料是一种介于软质(聚氨酯)和硬质(聚苯乙烯)泡沫塑料之间的闭孔结构的新型发泡塑料，具有优越的强韧性、弹性、挠曲性、耐磨性、耐化学腐蚀性、耐低温性和绝缘性好等一系列特性，可作为良好的绝缘、绝热、防震及浮力材料，广泛应用于工业、农业、建筑和交通运输等各个领域。高刚性聚乙烯发泡产品广泛用于地垫、汽车内饰、电子设备等领域，而且随着产品更新换代，对产品刚性提出了更高要求。传统提高聚乙烯泡沫刚性的方法主要包括添加聚丙烯、玻璃纤维、碳酸钙等以及增加交联度。由于聚丙烯的熔点较高，使得加工温度高，发泡剂容易分解，工艺实施困难。玻璃纤维、碳酸钙等无机填料与聚乙烯互溶性差，对产品刚性的提升有限，而且大量无机填料对发泡过程和产品的其它物理性能产品严重影响。交联度太大会导致发泡困难，无法满足合适发泡倍率。因此，如何提高聚乙烯泡棉材料的刚性，仍然是亟需解决的难题。
技术实现思路
为解决上述问题，本专利技术旨在提供一种辐照交联聚乙烯泡棉材料及其制备方法，以碳九石油树本文档来自技高网...

【技术保护点】
1.一种辐照交联聚乙烯泡棉材料的制备方法，其特征在于：包括步骤：首先，将以下组分混合后，加入到螺杆挤出机中进行混炼挤出得出母片；

【技术特征摘要】
1.一种辐照交联聚乙烯泡棉材料的制备方法，其特征在于：包括步骤：首先，将以下组分混合后，加入到螺杆挤出机中进行混炼挤出得出母片；然后，将上述步骤得到的母片进行电子辐照交联；电子辐照交联结束后，所得材料进行发泡处理，从而得到碳九石油树脂增强的聚乙烯泡棉材料。2.根据权利要求1所述的制备方法，其特征在于：所述的碳九石油树熔程为80～130℃。3.根据权利要求1所述的制备方法，其特征在于：各个组分含量如下：4.根据权利要求1所述的制备方法，其特征在于：螺杆挤出机的挤出温度为95～130℃。5.根据权利要求1所述的制备方法，其特征在于：螺杆挤出机的螺杆...

【专利技术属性】
技术研发人员：张轩，郭枫，梁学正，
申请(专利权)人：浙江万里新材料科技有限公司，
类型：发明
国别省市：浙江,33