The invention belongs to the technical field of hyaluronic acid, and in particular relates to a preparation method of crosslinked hyaluronic acid gel and a product thereof. Hyaluronic acid was crosslinked by sodium cross linked agent three sodium diphosphate in alkaline solution. Then the gel was cut into small pieces and soaked in acid solution to swell until the volume was constant. Then, a colorless, light yellow, transparent, granule free hyaluronic acid crosslinked hydrogel was obtained. The crosslinked gel has the advantages of simple preparation process, low production cost, high yield, and convenient amplification and production. The gel has good moisture retention and silky feeling, and is not sticky, and can be used in cosmetics and medical fields.
【技术实现步骤摘要】
一种三偏磷酸钠交联透明质酸凝胶的制备方法及其产品
技术介绍
透明质酸（HA）是由N个D-葡萄糖醛酸和N-乙酰葡糖胺双糖单位组成的酸性大分子粘多糖，又称为玻尿酸（Hyaluronan）、玻璃酸钠。由于透明质酸分子能携带500倍以上的水分，所以为当今所公认的最佳天然保湿成分，广泛应用于护肤品和化妆品中。但大分子量透明质酸用到化妆品中时，涂抹过程中易拉丝、起泥，在出汗或处在较潮湿的环境下，皮肤容易发黏，肤感不佳。交联或修饰的透明质酸在保留了天然透明质酸原有的良好生物相容性和保湿等功效的基础上，具有不同的流变性，可能会完善其在化妆品领域的用途，如改善肤感、抗皱、抗衰老。目前，BDDE（1,4-丁二醇二缩水甘油醚）和DVS（二乙烯基砜）为最常见的制备透明质酸凝胶的交联剂，但是这两种交联剂毒性较大，在使用时，必须通过透析或乙醇沉淀的方式将过量的交联剂除去，因此，凝胶的制备工艺相对复杂。然而三偏磷酸钠作为食品添加剂，也通常被报道为淀粉的有效交联剂，它是一种安全无毒的且对人类没有副作用的盐类物质，在美国通常被合法地用来交联食品级淀粉。使用三偏磷酸钠作为交联剂时，可以不用去除过量的交联剂...
【技术保护点】
1.一种三偏磷酸钠交联透明质酸凝胶的制备方法，其特征在于，通过以下步骤制备所得：（1）三偏磷酸钠加入碱性溶液中，搅拌至溶解；（2）透明质酸加入（1）的溶液中，快速搅拌，在25~50℃条件下反应4‑20 h；（3）将步骤（2）得到的透明质酸凝胶切成小块浸泡在酸性溶液中，搅拌，在15~30℃条件下，溶胀5‑12 h；小块直径为0.1‑0.2 cm；（4）待交联透明质酸凝胶小块溶胀至体积不变后，用纯化水洗涤2~3次，得到交联透明质酸凝胶。
【技术特征摘要】
1.一种三偏磷酸钠交联透明质酸凝胶的制备方法，其特征在于，通过以下步骤制备所得：（1）三偏磷酸钠加入碱性溶液中，搅拌至溶解；（2）透明质酸加入（1）的溶液中，快速搅拌，在25~50℃条件下反应4-20h；（3）将步骤（2）得到的透明质酸凝胶切成小块浸泡在酸性溶液中，搅拌，在15~30℃条件下，溶胀5-12h；小块直径为0.1-0.2cm；（4）待交联透明质酸凝胶小块溶胀至体积不变后，用纯化水洗涤2~3次，得到交联透明质酸凝胶。2.根据权利要求1所述的制备方法，其特征在于，三偏磷酸钠与透明质酸的质量比为0.075-0.30:1。3.根据权利要求1或2所述的制备方法，其特征在于，透明质酸为透明质酸及其盐；透明质酸及其盐的分子量为40-250万道尔顿，优选为50-150万道尔顿。4....
【专利技术属性】
技术研发人员：李霞，魏健，郭学平，王玉玲，石艳丽，郭文逸，耿凤，
申请(专利权)人：华熙生物科技股份有限公司，山东华熙海御生物医药有限公司，
类型：发明
国别省市：山东,37