The invention discloses a preparation method of hydrogen sulfide molecularly imprinted polymer with \sandwich\ structure. The hydrogen sulfide molecularly imprinted polymer with \sandwich\ structure is prepared by crosslinking polymerization on the surface of the carrier, using POMs@MOFs modified by heteropoly acid as carrier, water as template molecule, adding monomer, crosslinking agent and porogen, and the monomer. It contains double bonds and functional groups, which are carboxyl, amide, ester or pyridine groups. The polymer prepared by the invention acts as an adsorbent to realize the selective separation of hydrogen sulfide and carbon dioxide, and efficiently removes hydrogen sulfide.
【技术实现步骤摘要】
一种“三明治”结构的硫化氢分子印迹聚合物的制备方法
本专利技术涉及一种“三明治”结构的硫化氢分子印迹聚合物的制备方法，以及其作为吸附剂在去除硫化氢方面的应用，属于大气污染控制的技术范畴。
技术介绍
这里的陈述仅提供与本专利技术有关的背景信息，而不必然构成现有技术。硫化氢(H2S)是一种广泛存在于天然气、沼气、焦炉煤气及炼油废气等气体中的无色有毒的恶臭气体，也是预防空气污染需要去除的主要成分之一。硫化氢具有较强的酸性和腐蚀性，会严重腐蚀工业设备及管路，也是造成酸雨的主要污染物之一。此外，硫化氢的存在严重危害人体健康，低浓度的硫化氢对眼、呼吸系统及中枢神经系统都有影响如发热、发痒、头痛、头晕、呼吸困难，吸入少量高浓度硫化氢可于短时间内引发窒息、昏迷甚至死亡。世界职业安全与保健管理总署(OSHA)对硫化氢的浓度做了以下规定：浓度低于10ppm的硫化氢定义为低毒性，浓度介于10～30ppm的硫化氢为中等毒性，浓度高于30ppm的硫化氢定义为高毒性。专利技术人已知的硫化氢的去除方法主要有两种：(1)干法：碳材料、分子筛等吸附剂的吸附法，膜分离法，金属氧化物氧化法，辐照分解法...
【技术保护点】
1.一种硫化氢分子印迹聚合物的制备方法，其特征是，以水作为代替硫化氢的模板分子，进行本体聚合、悬浮聚合、乳液聚合、沉淀聚合或表面印迹聚合制备得到分子印迹聚合物。
【技术特征摘要】
1.一种硫化氢分子印迹聚合物的制备方法，其特征是，以水作为代替硫化氢的模板分子，进行本体聚合、悬浮聚合、乳液聚合、沉淀聚合或表面印迹聚合制备得到分子印迹聚合物。2.一种“三明治”结构的硫化氢分子印迹聚合物的制备方法，其特征是，以杂多酸改性的金属有机骨架为载体，以水为模板分子，加入单体、交联剂、致孔剂，在载体表面进行交联聚合反应，制备出具有“三明治”结构的硫化氢分子印迹聚合物，所述单体中含有双键和功能基团，所述功能基团为羧基、酰胺基团、酯基或吡啶基团。3.如权利要求2所述的制备方法，其特征是，所述金属有机骨架为对苯二甲酸和四氯化锆制备而成。4.如权利要求2所述的制备方法，其特征是，杂多酸改性的金属有机骨架的制备方法为：将苯二甲酸、四氯化锆和杂多酸加入至盐酸和二甲基甲酰胺中，进行溶剂热反应；优选的，四氯化锆与苯二甲酸的质量比为0.05～10:0.05～10；优选的，四氯化锆与杂多酸的质量比为0.05～10:0.05～10；优选的，四氯化锆、盐酸和二甲基甲酰胺添加比为0.05～10:0.1～10:1～100，g:mL:mL。5.如权利要求4所述的制备方法，其特征是，溶剂热反应的条件为100～300℃，反应时间为12～48h。6.如权利要求2所述的制备方法，其特征是，步骤为：将水和单体加入致...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。