The invention discloses a compressive heat preservation concrete, whose raw materials include cementing material, fine aggregate, coarse aggregate and accessories; the cementing material includes aluminate cement and white coal slag composite, and the weight ratio of aluminate cement and white coal slag composite is 200 to 400:35 to 65. The invention improves the thermal insulation performance of concrete, solves the difficult problem of poor thermal insulation of concrete which has been puzzled for many years, enhances the toughness of concrete, strengthens the compressive strength, effectively enhances the mechanical properties of concrete, makes the quality of concrete stable and durable, reduces the manufacturing cost of commercial concrete, improves the quality of commercial concrete, and further enlarges the overall competition. Potential.
【技术实现步骤摘要】
一种抗压保温混凝土
本专利技术涉及混凝土
，尤其涉及一种抗压保温混凝土。
技术介绍
混凝土，简称为“砼(tóng)”，是指由胶凝材料将集料胶结成整体的工程复合材料的统称。通常讲的混凝土一词是指用水泥作胶凝材料，砂、石作集料；与水(加或不加外加剂和掺合料)按一定比例配合，经搅拌、成型、养护而得的水泥混凝土，也称普通混凝土，它广泛应用于土木工程。现有混凝土保温性差，增韧效果差，严重影响混凝土使用寿命，建筑物寿命短。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种抗压保温混凝土，本专利技术提高了混凝土的保温性能，解决了多年困扰的凝土保温性差的难题，且增强了混凝土的韧性，增强了抗压强度，有效增强混凝土的力学性能，使混凝土质量稳定，耐久性长，并降低了商品混凝土的制造成本，提升了商品混凝土的品质，进一步扩大整体竞争优势。本专利技术提出的一种抗压保温混凝土，其原料包括：胶结料、细骨料、粗骨料、辅料；所述胶结料包括铝酸盐水泥、白煤渣复合物，而铝酸盐水泥、白煤渣复合物的重量比为200-400：35-65。优选地，细骨料为铝粉和/或重晶石粉。优选地，细骨料包括铝粉、...
【技术保护点】
1.一种抗压保温混凝土，其特征在于，其原料包括：胶结料、细骨料、粗骨料、辅料；所述胶结料包括铝酸盐水泥、白煤渣复合物，而铝酸盐水泥、白煤渣复合物的重量比为200‑400：35‑65。
【技术特征摘要】
1.一种抗压保温混凝土，其特征在于，其原料包括：胶结料、细骨料、粗骨料、辅料；所述胶结料包括铝酸盐水泥、白煤渣复合物，而铝酸盐水泥、白煤渣复合物的重量比为200-400：35-65。2.根据权利要求1所述的抗压保温混凝土的制备工艺，其特征在于，细骨料为铝粉和/或重晶石粉。3.根据权利要求2所述的抗压保温混凝土的制备工艺，其特征在于，细骨料包括铝粉、重晶石粉；铝粉、重晶石粉的重量比为12-40：40-100。4.根据权利要求1所述的抗压保温混凝土的制备工艺，其特征在于，粗骨料为废弃塑料颗粒、煤渣、麦饭石粉、硅藻土、煤矸石、重质碳酸钙中至少一种。5.根据权利要求4所述的抗压保温混凝土的制备工艺，其特征在于，粗骨料按重量份包括20-50份废弃塑料颗粒、24-45份煤渣、5-12份麦饭石粉、10-19份硅藻土、20-30份煤矸石、5-18份重质碳酸钙。6...
【专利技术属性】
技术研发人员：朱泽松，陈小瑞，张国富，
申请(专利权)人：滁州职业技术学院，
类型：发明
国别省市：安徽,34