The invention belongs to the technical field of non-ferrous metal metallurgy, in particular to a method for deep leaching of antimony from complex antimony-containing materials. By adding some compound reagent in the pretreatment process of complex antimony-containing materials, the leaching rate of antimony in the subsequent leaching process of complex antimony-containing materials can be significantly improved, which is beneficial to the effective enrichment of antimony elements and the efficient utilization of antimony resources. The method has the advantages of simple operation, low cost and obvious effect in the treatment of complex antimony-containing materials. The antimony pretreated residue can be used in the conventional antimony leaching process. The yield of antimony can be stable more than 80%, and the treatment process is more economical and efficient.
【技术实现步骤摘要】
一种深度浸出复杂含锑物料中锑元素的方法
本专利技术属于有色金属冶金
，尤其涉及一种深度浸出复杂含锑物料中锑元素的方法。
技术介绍
金属锑由于其性质的特点除用于电镀外，很少单独使用，多以其他金属为基体配成各种各样的合金。锑业的发展与印刷业的发展分不开，因发现铅基锑锡合金熔点低，易浇铸，铸成的铅字轮廓清晰，经久耐用，生产印刷合金而开创了锑在工业应用上的新纪元。19世纪初，锑作为铅的增硬剂用于制造榴霰弹，使铅丸在炮弹爆炸时易破裂，增加杀伤力，所以第一次世界大战中称锑为“战争金属”。20世纪以来用含锑的铅做蓄电池栅板、铅板及接头零件，使锑的用量大增，并随着现代交通事业的发展而发展。蓄电池广泛应用于飞机、轮船、铁路机车、汽车、拖拉机和邮电通讯等。1939年美国人专利技术的巴比特耐磨铅锑合金，用于做轴承的轴瓦，又称轴承合金，在应用过程中不断发展。现在已有锡基、铅基、锌基和铝锑镁的巴氏合金用于各种不同用途。此外，锑青铜即以锑代锡的锑铜合金可制造受重载荷的齿轮电机的轴衬，铅锑合金可做成电缆护套，锑还可用于配制各种焊料等。纯度大于99.9994％的锑，用于制造远红外装置、金属...
【技术保护点】
1.一种深度浸出复杂含锑物料中锑元素的方法，其特征在于：该方法的步骤为：S1:在复杂含锑物料预处理过程中加入复合试剂，备用；S2：在常压下持续搅拌，并加热进行反应，反应过程中体系酸度以硫酸计为40‑160g/l；反应结束后过滤，得到锑预处理后渣和处理后液；锑预处理后渣用常规浸锑方法进行锑浸出操作，锑浸出率高。
【技术特征摘要】
1.一种深度浸出复杂含锑物料中锑元素的方法，其特征在于：该方法的步骤为：S1:在复杂含锑物料预处理过程中加入复合试剂，备用；S2：在常压下持续搅拌，并加热进行反应，反应过程中体系酸度以硫酸计为40-160g/l；反应结束后过滤，得到锑预处理后渣和处理后液；锑预处理后渣用常规浸锑方法进行锑浸出操作，锑浸出率高。2.根据权利要求1所述的方法，其特征在于，所述S1中：加入的复合试剂量为：复合试剂量与溶液体积关系为5-50克试剂/升溶液。3.根据权利要求1所述...
【专利技术属性】
技术研发人员：杨兴文，涂相林，张飞，邹志武，肖亚松，张凡，钟志燕，罗钊荣，邓成武，