The invention discloses a preparation method of surfactant for cutting fluid, which includes steps 1: alkali refining of soybean oil to remove polite fatty acids; step 2: transesterification of soybean oil after alkali refining with methanol to obtain soybean oil methyl ester; step 3: aminolysis of soybean oil methyl ester and diethanolamine after transesterification to obtain soybean oil. Alkanolamide. Through the above way, the invention provides a preparation method of surfactant for cutting fluid. The surfactant prepared by the method greatly increases its production rate by changing the feed ratio and other conditions, and does not pollute the environment.
【技术实现步骤摘要】
一种切削液用表面活性剂的制备方法
本专利技术涉及切削液领域,尤其涉及一种切削液用表面活性剂的制备方法。
技术介绍
切削液是金属切削加工的重要的配套材料,使用金属切削液的目的就是降低切削力及刀具与工件之间的摩擦,及时带走切削区内产生的热量以降低切削温度,减少刀具磨损,提高刀具耐用度,从而提高生产效率,改善工件表面粗糙度,保证工件加工精度,从而达到最佳经济效果,切削液制备过程中需要非离子型表面活性剂,大豆油烷醇酰胺是一种良好的非离子型表面活性剂,然后现有的制备大豆油烷醇酰胺的产率不高,而且实验时不环保,产生的副产物对环境造成了污染。
技术实现思路
本专利技术主要解决的技术问题是提供一种切削液用表面活性剂的制备方法。为解决上述技术问题,本专利技术采用的一个技术方案是:一种切削液用表面活性剂的制备方法,具体步骤包括:步骤一:对大豆油进行碱炼,去除有礼的脂肪酸;步骤二:将步骤一碱炼后的大豆油与甲醇进行酯交换,得到大豆油甲酯;步骤三:将步骤二酯交换后大豆油甲酯与二乙醇胺进行胺解,得到大豆油烷醇酰胺。在本专利技术一个较佳实施例中,所述步骤一中选用17%的氢氧化钠溶液进行碱炼。在本专利技术一个较佳实施例中,所述步骤三中大豆油甲酯与乙二醇胺的量比为1:3。本专利技术的有益效果是:本专利技术一种切削液用表面活性剂的制备方法,该方法制备的表面活性剂通过改变投料比等条件,大大增加了其生产率,而且不会对环境产生污染。具体实施方式下面对本专利技术的较佳实施例进行详细阐述,以使本专利技术的优点和特征能更易于被本领域技术人员理解,从而对本专利技术的保护范围做出更为清楚明确的界定。本专利技术实 ...
【技术保护点】
1.一种切削液用表面活性剂的制备方法,其特征在于,具体步骤包括:步骤一:对大豆油进行碱炼,去除有礼的脂肪酸;步骤二:将步骤一碱炼后的大豆油与甲醇进行酯交换,得到大豆油甲酯;步骤三:将步骤二酯交换后大豆油甲酯与二乙醇胺进行胺解,得到大豆油烷醇酰胺。
【技术特征摘要】
1.一种切削液用表面活性剂的制备方法,其特征在于,具体步骤包括:步骤一:对大豆油进行碱炼,去除有礼的脂肪酸;步骤二:将步骤一碱炼后的大豆油与甲醇进行酯交换,得到大豆油甲酯;步骤三:将步骤二酯交换后大豆油甲酯与二乙醇胺进行胺解,得到大豆油烷醇...