The present invention relates to an environmentally friendly wear-resistant PVC pipe. The components of the said environmentally friendly wear-resistant PVC pipe are as follows: 30 40 copies of polyvinyl chloride, 15 20 copies of toluene diisocyanate, 20 25 copies of hexamethylene diisocyanate, 5 10 copies of graphite powder, 10 15 copies of glass fiber, 3 7 copies of epoxy soybean oil, 2 5 copies of potassium humate, 0.5 1.3 copies of scratch-resistant agent, 0.5.5 cop _0.9 copies and 1_2 copies of cosolvent. The invention has the advantages of low production cost, good wear resistance, more environmental protection than the traditional PVC pipe, and broad application prospects.
【技术实现步骤摘要】
一种环保型耐磨PVC管
本专利技术涉及PVC管材
，尤其涉及一种环保型耐磨PVC管。
技术介绍
现有的PVC管材耐磨性一般，且在加工、使用过程中受热、光、氧的作用后聚氯乙烯主链易发生裂解，发生老化现象，因此不可以在恶劣条件及较高温度下使用，很大程度上影响了PVC管材的应用。
技术实现思路
为解决上述问题，本专利技术提供了一种环保型耐磨PVC管。本专利技术的技术方案如下：一种环保型耐磨PVC管，其特征在于：所述环保型耐磨PVC管的组分按照重量份如下所示：聚氯乙烯30-40份，甲苯二异氰酸酯15-20份，六亚甲基二异氰酸酯20-25份，石墨粉5-10份，玻璃纤维10-15份，环氧大豆油3-7份，腐植酸钾2-5份，抗划伤剂0.5-1.3份，耐黄变剂0.5-0.9份，助溶剂1-2份。进一步的，所述耐黄变剂为硫代二丙酸双(十八)醇酯、六甲基磷酸三酰胺中的一种。进一步的，所述助溶剂为水杨酸钠，对氨基苯甲酸中的一种。进一步的，所述玻璃纤维的粒径为0.3-0.6μm。借由上述方案，本专利技术至少具有如下优点：本专利技术制作成本低廉，耐磨效果好，同时比传统PVC管更加环保，具有广阔的应用前景。具体实施方式下面结合实施例对本专利技术的技术方案作如下详细说明。实施例1一种环保型耐磨PVC管，其特征在于：所述环保型耐磨PVC管的组分按照重量份如下所示：聚氯乙烯37份，甲苯二异氰酸酯19份，六亚甲基二异氰酸酯21份，石墨粉6份，玻璃纤维12份，环氧大豆油4份，腐植酸钾3份，抗划伤剂1.3份，六甲基磷酸三酰胺0.7份，水杨酸钠1.3份。其中，所述玻璃纤维的粒径为0.3-0.6μm。...
【技术保护点】
1.一种环保型耐磨PVC管，其特征在于：所述环保型耐磨PVC管的组分按照重量份如下所示：聚氯乙烯30‑40份，甲苯二异氰酸酯15‑20份，六亚甲基二异氰酸酯20‑25份，石墨粉5‑10份，玻璃纤维10‑15份，环氧大豆油3‑7份，腐植酸钾2‑5份，抗划伤剂0.5‑1.3份，耐黄变剂0.5‑0.9份，助溶剂1‑2份。
【技术特征摘要】
1.一种环保型耐磨PVC管，其特征在于：所述环保型耐磨PVC管的组分按照重量份如下所示：聚氯乙烯30-40份，甲苯二异氰酸酯15-20份，六亚甲基二异氰酸酯20-25份，石墨粉5-10份，玻璃纤维10-15份，环氧大豆油3-7份，腐植酸钾2-5份，抗划伤剂0.5-1.3份，耐黄变剂0.5-0.9份，助溶剂1-2份。2.根...
【专利技术属性】
技术研发人员：陈云，
申请(专利权)人：丹阳市贝尔特橡塑制品有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。