The invention relates to the technical field of building materials, in particular to a ceramic tile glue and its preparation method, including the following raw material components: 25-38 parts of Huanghe sediment, 20-35 parts of dry sand, 10-25 parts of sludge, 12-20 parts of cement, 2-10 parts of rosin saponification, 1-5 parts of water-soluble silicate and 1-5 parts of cocoa. Re-dispersed latex powder and 0.2-2 phr micro-expander. The ceramic tile adhesive provided by the invention has high bonding strength, water resistance, good corrosion resistance, heat aging resistance (70 C), can withstand the test of alternation of drying and wetting and freezing and thawing, and thoroughly solves the problems of pan-alkali, empty drum and spalling of ceramic tile.
【技术实现步骤摘要】
一种瓷砖胶及其制备方法
本专利技术涉及建筑材料
，具体涉及一种瓷砖胶及其制备方法。
技术介绍
瓷砖胶又称陶瓷砖粘合剂，主要用于粘贴瓷砖、面砖、地砖等装饰材料，广泛适用于内外墙面、地面、浴室、厨房等建筑的饰面装饰场所。其主要特点是粘接强度高、耐水、耐冻融、耐老化性能好及施工方便，是一种非常理想的粘结材料。瓷砖胶中含有多种添加剂，具体是瓷砖胶的功能性。一般瓷砖胶中添加了提供保水和增稠作用的纤维素醚，以及提供增加瓷砖胶粘接力的乳胶粉，乳胶粉最常见的有醋酸乙烯/乙烯酯共聚物、月桂酸乙烯/乙烯/氯乙烯共聚物、丙烯酸类等添加剂，乳胶粉的添加能够大大增加瓷砖胶的柔性以及改善应力的作用，增加柔韧性能。另外一些特殊功能要求的瓷砖胶则添加其他类添加剂，比如添加木质纤维能够提高砂浆的抗开裂性和提高开放时间，添加改性淀粉醚提供砂浆抗滑移性能，添加早强剂使得瓷砖胶更快提升强度，添加憎水剂以降低吸水率提供防水作用等。然而现有技术中采用的瓷砖胶，碱性高，容易腐蚀瓷砖，造成砖面变色；并且普通硅酸盐水泥硬度高，施工后砖面易开裂；在高温环境下质量性能不稳定，在变形的基材或铁板上无法粘贴。专利技...
【技术保护点】
1.一种瓷砖胶，其特征在于，包括以下重量份数的原料组分：包括以下重量份数的原料组分：25～38份的黄河泥沙、20～35份的干细沙、10～25份的淤泥、12～20份的水泥、2～10份的松香皂化物、1～5份的水溶性硅酸盐、1～5份的可再分散乳胶粉和0.2～2份的微膨胀剂。
【技术特征摘要】
1.一种瓷砖胶，其特征在于，包括以下重量份数的原料组分：包括以下重量份数的原料组分：25～38份的黄河泥沙、20～35份的干细沙、10～25份的淤泥、12～20份的水泥、2～10份的松香皂化物、1～5份的水溶性硅酸盐、1～5份的可再分散乳胶粉和0.2～2份的微膨胀剂。2.根据权利要求1所述的瓷砖胶，其特征在于，所述松香皂化物包括重量份数为50～70份松香、10～25份的氢氧化纳和80～120份的水。3.根据权利要求1所述的瓷砖胶，其特征在于，所述微膨胀剂为钙镁氧化物、硫铝酸钙中的一种或几种的混合物。4.根据权利要求1所述的瓷砖胶，其特征在于，所述可再分散乳胶粉为苯乙烯-丙烯酸共聚乳胶粉或乙烯-醋酸乙烯共聚乳胶粉。5.根据权利要求1所述的瓷砖胶，其特征在于，所述瓷砖胶还包括以下重量份数的原料组分：0.5～4份的减水剂、0.2～3份的超塑化剂、1～5份的增稠剂和0.1～2份的抗裂纤维。6.根据权利要求5所述的瓷砖胶，其特征在于，所述减水剂为三聚氰胺和/或聚羧酸；所述超塑化剂包括醋酸乙烯-乙烯共聚物干粉、聚乙烯干粉、聚丙烯酸酯干粉中的一种或几种的混合物；所...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。