The invention belongs to the field of material preparation technology, and relates to a composite material forming process. In order to solve the existing composite materials (mainly those including the surface layer and the core layer in the surface layer, and the core layer is generally foam, the surface layer is generally the composite material of the fabric), the product is generally prepared by the molding process, such as hand paste or prepreg molding, etc., and the product has the product quality (main body). The invention provides a composite material forming process, which uses two different methods to prepare the inner and outer layers of the composite material respectively. The technical scheme of the invention can effectively solve the above technical problems.
【技术实现步骤摘要】
一种树脂复合材料的制备方法
本专利技术属于材料制备
，涉及一种复合材料成型工艺，所述复合材料包括表层以及位于表层内的芯层，所述芯层一般为泡沫，表层为织物。
技术介绍
对于一些复合材料，例如厚度较厚的复材制品，一般10mm以上，例如斜坡板、床板、冲浪板、墙板、座椅、风电叶片等等，普遍采用双层结构，即表层以及位于表层内的芯层，其制备工艺例如手糊成型及预浸料模压成型工艺均已被广泛应用，但各自存在缺点。手糊成型工艺，生产效率低、速度慢、生产周期长，产品质量不够稳定。由于操作人员技能水平不同及制作环境条件的影响故产品质量稳定性差；生产环境差，气味大，加工时粉尘多，而预浸料模压成型工艺，表面效果容易存在缺陷，易造成针孔和色差。
技术实现思路
本专利技术所要解决的技术问题在于现有一些复合材料(主要是那些包括表层以及位于表层内的芯层，且芯层一般为泡沫，表层一般为织物的复合材料)普遍采用如手糊或预浸料模压等成型工艺制备，制成的产品存在产品质量(主要体现在产品的物理性能上)不够稳定或产品表面存在针孔和色差等问题，并针对这些问题提供一种复合材料成型工艺。本专利技术通过第一技术方案解决...
【技术保护点】
1.一种树脂复合材料的制备方法，第一树脂调配物一般包括如下组分：树脂、用于树脂固化的固化剂以及提升树脂固化速度的促进剂，其中树脂和固化剂为第一树脂调配物的必要成分，而促进剂为第一树脂调配物的可选成分，对于树脂，由于环氧树脂本身力学性能较好，粘接性较好，本具体实施方式一般选用环氧树脂，通常不同厂商不同牌号的环氧树脂力学性能不同，可根据产品实际用途，选择适合产品的环氧树脂，而固化剂可以是现有树脂固化剂。
【技术特征摘要】
1.一种树脂复合材料的制备方法，第一树脂调配物一般包括如下组分：树脂、用于树脂固化的固化剂以及提升树脂固化速度的促进剂，其中树脂和固化剂为第一树脂调配物的必要成分，而促进剂为第一树脂调配物的可选成分，对于树脂，由于环氧树脂本身力学性能较好，粘接性较好，本具体实施方式一般选用环氧树脂，通常不同厂商不同牌号的环氧树...