The invention relates to an ultra-bright polyester pre-oriented yarn and a preparation method thereof. The preparation method is as follows: firstly, the mixture of phthalic acid, ethylene glycol, silicon-containing diol in the main chain, fluorine-containing dibasic acid, 2,2,3,4,5,5 hexamethyl 3,4 hexanediol and doped ZrO 2 powder is homogeneous, then esterification reaction and polycondensation reaction are carried out to prepare modified polyester, and then the triangular spinneret is used to prepare modified polyester according to POY. Modified polyester POY filament was prepared by melting modified polyester, i.e. super bright polyester preferred filament. The dyeing rate, K/S value and color fastness of the ultrabright polyester preferred yarn are high, and the natural degradation rate is fast. The dyeing performance of the fiber is improved by adding 2,2,3,4,5,5_hexamethyl_3,4_hexanediol and silicon-containing diol in the main chain. The addition of fluorine-containing dicarboxylic acid and doped modified ZrO2 powder improves the degradation performance of the polyester fiber; the dyeing performance and degradation performance of the product are excellent.
【技术实现步骤摘要】
超亮光涤纶预取向丝及其制备方法
本专利技术属于聚酯纤维
，涉及一种超亮光涤纶预取向丝及其制备方法。
技术介绍
涤纶(即PET纤维)是我国聚酯纤维的商品名称，是合成纤维中的一个重要品种。随着涤纶生产规模的扩大，生产技术也得到了很大的提高，由刚开始的常规化产品的生产，逐渐向高技术、功能化以及差别化纤维等生产方向发展，生产差别化纤维产品主要有两种途径：一是采用新单体或合成方法制造新的高聚物，这一方法的主要技术有聚合物改性技术、超细纤维制造技术、异形纤维制造技术和复合纺丝技术等，另一种方法是通过对现有的纤维进行改性，使其获得新的性能，而采用后一方法有投资少、见效快等优点，因此对聚酯的改性也变得尤为的重要，聚酯改性目的除了对普通聚酯性能进行优化外，主要是通过改性手段赋予新型聚酯差别化的功能性特征。超亮光，主要是通过熔融纺丝、截面异形化，赋予了涤纶纤维真丝般的光泽和手感、织物明亮感以及柔和高雅的丝绸光感，除具有优良的光学特性外，由于异形截面的纤维外形不规则，纤维之间的排列无法紧密，空隙相应增大，从而织物手感更厚实，蓬松性、透气性好，具有超亮闪光效果。超亮光异形涤纶丝广泛...
【技术保护点】
1.超亮光涤纶预取向丝的制备方法，其特征是：采用三角形喷丝板按POY工艺由改性聚酯熔体制得改性聚酯POY丝，即得超亮光涤纶预取向丝；所述改性聚酯的制备方法为：将对苯二甲酸、乙二醇、主链含硅的二元醇、含氟二元酸、2,2,3,4,5,5‑六甲基‑3,4‑己二醇和掺杂改性的ZrO2粉体混合均匀后先后进行酯化反应和缩聚反应；2,2,3,4,5,5‑六甲基‑3,4‑己二醇的结构式如下：
【技术特征摘要】
1.超亮光涤纶预取向丝的制备方法，其特征是：采用三角形喷丝板按POY工艺由改性聚酯熔体制得改性聚酯POY丝，即得超亮光涤纶预取向丝；所述改性聚酯的制备方法为：将对苯二甲酸、乙二醇、主链含硅的二元醇、含氟二元酸、2,2,3,4,5,5-六甲基-3,4-己二醇和掺杂改性的ZrO2粉体混合均匀后先后进行酯化反应和缩聚反应；2,2,3,4,5,5-六甲基-3,4-己二醇的结构式如下：主链含硅的二元醇为二甲基硅二醇、二甲基二苯基二硅氧烷二醇或四甲基二硅氧烷二醇，含氟二元酸为2,2-二氟-1,3-丙二酸、2,2-二氟-1,4-丁二酸、2,2-二氟-1,5-戊二酸或2,2,3,3-四氟-1,4-丁二酸；ZrO2掺杂改性的过程为：首先将含金属离子Mx+的溶液与含Zr4+的溶液混合均匀，然后滴加沉淀剂至混合液的pH值为9～10，最后煅烧沉淀产物；金属离子Mx+为Mg2+、Li+和Zn2+中的一种以上。2.根据权利要求1所述的超亮光涤纶预取向丝的制备方法，其特征在于，所述含金属离子Mx+的溶液的浓度为1～2wt％，溶剂为水，溶液中的阴离子为NO3-；所述含Zr4+的溶液为浓度20～25wt％的ZrO2的溶液，溶剂为硝酸；所述沉淀剂为浓度2mol/L的氨水；沉淀开始时，混合液中金属离子Mx+与Zr4+的摩尔比为5～8:100；所述煅烧前对沉淀产物进行洗涤和干燥，干燥的温度为105～110℃，时间为2～3h；所述煅烧的过程为：首先升温至400℃后保温2～3h，然后升温至700℃后保温1～2h，最后在空气中冷却；ZrO2在掺杂改性后进行粉碎得到平均粒径小于0.5微米的粉体；改性聚酯的数均分子量为25000～30000，分子量分布指数为1.8～2.2。3.根据权利要求2所述的超亮光涤纶预取向丝的制备方法，其特征在于，所述2,2,3,4,5,5-六甲基-3,4-己二醇的合成方法为：将醋酸钯和二甲基二叔丁基乙烯混合均匀后，在加热和搅拌条件下，加入质量浓度为10～15％的双氧水溶液，在温度为70～75℃的条件下反应3～4h，经冷却、结晶和精制得到2,2,3,4,5,5-六甲基-3,4-己二醇，所述二甲基二叔丁基乙烯、双氧水溶液和醋酸钯的质量比为1:1.5～2.0:0.0153。4.根据权利要求3所述的超亮光涤纶预取向丝的制备方法方法，其特征在于，所述改性聚酯的制备步骤如下：(1)酯化反应；将对苯二甲酸、乙二醇、主链含硅的二元醇、含氟二元酸和2,2,3,4,5,5-六甲基-3,4-己二醇配成浆料，加入掺杂改性的ZrO2粉体、催化剂和稳定剂混合均匀后，在氮气氛围中加压进行酯化反应，加压压力为常压～0.3MPa，酯化反应的温度为...
【专利技术属性】
技术研发人员：汤方明，周文龙，张元华，
申请(专利权)人：江苏恒力化纤股份有限公司，
类型：发明
国别省市：江苏,32