The present invention relates to an electrolyte plasma polishing solution for aluminium alloy and its polishing process. The polishing solution comprises the following components: the concentration of ferric sulfate is 2%-2.5% mol/L, the concentration of ammonium sulfate is 2% mol/L, a number of additives, and the rest is water. The invention improves the performance of the polishing fluid through experimental research and optimization of the formulation, and provides a polishing process using the polishing fluid. By adopting the scheme of the invention, the polishing time is short, the effect is obvious, and the use period is long; the polishing liquid can not produce harmful gases and does not pollute the environment.
【技术实现步骤摘要】
一种铝合金的电解质等离子抛光液及抛光工艺
本专利技术涉及抛光液领域，具体涉及一种铝合金的电解质等离子抛光液及抛光工艺。
技术介绍
电解质-等离子加工技术是一种新型现代化、高效能、对复杂形金属部件进行表面加工的技术。该技术适用于对金属表面抛光，消除毛刺，磨钝尖刃，清理焊接缝，清除材料表面的氧化色，氧化皮和污渍，表面除油等。在该抛光体系下电极(抛光工件)、放电介质、气层和抛光液四相共同作用，通过放电去除表面材料，区别于传统等离子体抛光的化学去除，也区别于电解抛光体系下的电极、电解液的两相相互作用，利用电解液的电化学溶解完成抛光。抛光液使用低浓度的中性盐溶液对环境几乎没有污染，抛光质量和效率都是传统抛光方法难以达到的。电解质-等离子加工是一种复杂的电化学、等离子化学过程，电解液单因素参数对样件去除速度、表面加工质量等具有非常重要的影响，不同的材料进行电解质-等离子加工所需要的电解液参数也不尽相同。对于铝合金，使用现有的抛光液配方抛光效果不理想，存在氧化膜影响抛光后铝合金表面光亮度的问题。因此，本专利技术将从铝合金抛光液配方的角度进行研究，以改善铝合金的抛光效果。铝合金的...
【技术保护点】
1.一种铝合金的电解质等离子抛光液，其特征在于：抛光液中包括以下组份：硫酸铁浓度为2％～2.5％mol/L，硫酸铵浓度为2％mol/L，添加剂若干，其余为水。
【技术特征摘要】
1.一种铝合金的电解质等离子抛光液，其特征在于：抛光液中包括以下组份：硫酸铁浓度为2％～2.5％mol/L，硫酸铵浓度为2％mol/L，添加剂若干，其余为水。2.根据权利要求1所述的铝合金的电解质等离子抛光液，其特征在于：所述添加剂包括PEG600浓度为1％mol/L、柠檬酸浓度为3％mol/L、EDTA浓度为0.07％mol/L、葡萄糖酸钠浓度为5％mol/L。3.采用权利要求1或2所述的铝合金的电解质等离子抛光液的抛光工艺，其特征在于：包括以下步骤：a)将铝合金材料进行抛光前处理；b)将权利要求1或2所述的抛光液倒入电解质等离子抛光机的抛光槽内，设定加热抛光液温度，设定抛光时间；c)将铝合金材料置于...
【专利技术属性】
技术研发人员：赵锦芝，姜爱冰，刘程浩，刘远韬，王诗兆，肖进，索来春，
申请(专利权)人：南京工程学院，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。