The invention discloses an automobile brake pad and a preparation method thereof. The automobile brake pad comprises the following components by weight: Benzoxazine Resin 10_20, porous aluminium powder 5_10, porous copper powder 5_10, rubber powder 5_10, graphite powder 5_10, barium sulfate 25_50, alumina 5_10 and carbon fiber 10_20. The brake pad formulation which can be printed in 3D has high fluidity and does not produce gas when cured, so it can be used to produce friction pad in the process of 3D printing. Moreover, the special 3D printing device is used to print the brake pads, so it can not be restricted by the die. A single device can produce all kinds of friction pads. Because of its small heating device, compared with the conventional production mode, it saves a lot of power consumption.
【技术实现步骤摘要】
一种汽车刹车片及其制备方法
本专利技术属于摩擦材料
，具体涉及一种汽车刹车片及其制备方法。
技术介绍
汽车刹车片的一般制备工艺是把粘接剂、增强纤维和填料混拌后，经过加热加压固化成型，该方法具备工艺简便的优点，然而其限制在于对于不同的摩擦片品种需要不同模具，因而在生产中需要倒换模具，生产效率较低，另外当产品型号较多时，需要准备较多的模具，增加了工装投入。另外，在成型过程中要得到一定的制品密度，需要大吨位压机。而为了使材料中的粘接剂树脂固化，需要对整个模具加热，从而消耗大量电力。
技术实现思路
针对现有技术中存在的技术问题，本专利技术提供一种汽车刹车片及其制备方法。生产该汽车刹车片只需要一台小型3D打印装置即能生产各种型号尺寸的刹车片，不需要大吨位压机和模具，同时还节约了大量电力消耗。为解决上述技术问题，本专利技术采用的技术方案是：一种汽车刹车片，所述汽车刹车片按重量份包括以下各组分：苯并噁嗪树脂10-20份、多孔铝粉5-10份、多孔铜粉5-10份、橡胶粉5-10份、石墨粉5-10份、硫酸钡25-50份、氧化铝5-10份及碳纤维10-20份。上述方案中，所述汽车刹车...
【技术保护点】
1.一种汽车刹车片，其特征在于，所述汽车刹车片按重量份包括以下各组分：苯并噁嗪树脂10‑20份、多孔铝粉5‑10份、多孔铜粉5‑10份、橡胶粉5‑10份、石墨粉5‑10份、硫酸钡25‑50份、氧化铝5‑10份及碳纤维10‑20份。
【技术特征摘要】
1.一种汽车刹车片，其特征在于，所述汽车刹车片按重量份包括以下各组分：苯并噁嗪树脂10-20份、多孔铝粉5-10份、多孔铜粉5-10份、橡胶粉5-10份、石墨粉5-10份、硫酸钡25-50份、氧化铝5-10份及碳纤维10-20份。2.如权利要求1所述的汽车刹车片，其特征在于，所述汽车刹车片按重量份包括以下各组分：苯并噁嗪树脂20份、多孔铝粉10份、多孔铜粉10份、橡胶粉5份、石墨粉5份、硫酸钡25份、氧化铝5份及碳纤维20份。3.如权利要求1所述的汽车刹车片，其特征在于，所述汽车刹车片按重量份包括以下各组分：苯并噁嗪树脂10份、多孔铝粉5份、多孔铜粉5份、橡胶粉10份、石墨...
【专利技术属性】
技术研发人员：吴耀庆，
申请(专利权)人：湖北飞龙摩擦密封材料股份有限公司，
类型：发明
国别省市：湖北,42