The invention relates to a preparation method of magnesium-based cementitious material. The specific steps are as follows: adding waste hydrochloric acid solution into magnesium sulfate solution by weight, stirring evenly, then adding magnesium oxide and polycrystalline silicon waste residue to stir into slurry, and then pouring into cement products. The invention uses waste hydrochloric acid and polycrystalline silicon waste residue as modifier to prepare magnesium cement, which can obviously improve the water resistance of the material. The process is simple, which solves the disadvantage of poor water resistance of magnesium cement and reduces the production cost of building materials enterprises. At the same time, it realizes the resource utilization of waste hydrochloric acid and polysilicon slag, and reduces the environmental pollution and treatment costs.
【技术实现步骤摘要】
一种耐水性镁基胶凝材料的制备方法
本专利技术涉及一种耐水性镁基胶凝材料的制备方法，特别涉及一种以废盐酸、多晶硅废渣为改性剂提高镁基水泥建筑材料耐水性的方法。
技术介绍
镁水泥制品具有体积稳定性高、质轻、耐火、碱度低、装饰效果好、不吸潮反卤、对钢筋腐蚀作用小等优点，使其在制作装饰、装修材料上更具优势。但其耐水性差的缺陷，限制了应用。因此，研究开发耐水性的镁基胶凝材料，势在必行。为了解决镁水泥耐水性差的问题，外加剂的加入成为目前研究比较广泛的方法。多晶硅废渣是生产多晶硅过程中产生的固体废弃物，目前国内多晶娃废渣主要以堆存和简易填埋的方式处理，不仅占用大量土地，并具有一定的毒害性，如果不能及时加以合理处置和安全利用，会造成环境污染和资源浪费，这已经成为多晶硅生产企业非常棘手的问题。盐酸是一种常用的化工原料，广泛应用于化工、钢铁、电镀和钢铁结构件的酸洗生产，每年产生大量的含盐酸废水。本专利技术以废盐酸、多晶硅废渣为改性剂，解决镁水泥耐水性差的问题，使难以处理的工业废渣物尽其用。
技术实现思路
本专利技术提供了一种耐水性镁基胶凝材料的制备方法，以废盐酸和多晶硅废渣作为复合改性剂...
【技术保护点】
1.一种耐水性镁基胶凝材料的制备方法，其特征在于：先配制硫酸镁溶液，按重量将废盐酸溶液加入到硫酸镁溶液中搅拌均匀，然后加入多晶硅废渣搅拌均匀，充分反应后，再加入氧化镁制成浆料，然后浇筑成型制成镁水泥制品。
【技术特征摘要】
1.一种耐水性镁基胶凝材料的制备方法，其特征在于：先配制硫酸镁溶液，按重量将废盐酸溶液加入到硫酸镁溶液中搅拌均匀，然后加入多晶硅废渣搅拌均匀，充分反应后，再加入氧化镁制成浆料，然后浇筑成型制成镁水泥制品。2.根据权利要求1所述的一种耐水性镁基胶凝材料的制备方法，其特征在于：所述废盐酸、多晶硅废渣、硫酸镁和氧化镁的比例为1:(1.3～3....
【专利技术属性】
技术研发人员：郝亚菲，赵风清，李超，张志国，田晓华，刘东基，刘少杰，范天本，
申请(专利权)人：河北科技大学，
类型：发明
国别省市：河北,13
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。