一种利用废旧轮胎料制成的保温砂浆制造技术

本发明专利技术属于建筑材料领域，提出一种利用废旧轮胎料制成的保温砂浆，原料按重量份包括：镁铝水泥25‑35份，建筑石灰10‑15份，自来水20‑30份，中砂5‑10份，经粉碎清洗后粒径不超过50目的废旧轮胎料颗粒10‑15份，水交联性聚乙烯3‑5份，丙酮3‑5份；具有较好的隔热性能和耐久性；有效利用废旧轮胎料，减少环境污染；抗冲击性及抗裂性好，长期使用无起泡、脱落现象，可大规模推广应用。

A Thermal-insulating Mortar Made of Waste Tire Material

The invention belongs to the field of building materials, and proposes a thermal insulation mortar made of waste tire materials. The raw materials include 25 35 portions of magnesia-aluminium cement, 10 15 portions of building lime, 20 30 portions of tap water, 5 10 portions of medium sand, 10 15 portions of waste tire particles with particle size not exceeding 50 purposes after crushing and cleaning, 3 5 portions of water-crosslinked polyethylene and 3 5 portions of acetone. Thermal insulation and durability; the effective use of waste tire materials to reduce environmental pollution; impact resistance and crack resistance, long-term use without foaming, shedding phenomenon, can be widely applied.

【技术实现步骤摘要】
一种利用废旧轮胎料制成的保温砂浆
本专利技术属于建筑材料领域，具体涉及一种醇酸树脂复合外墙涂料。
技术介绍
汽车工业的高速发展产生了大量的轮胎废料，轮胎是一种橡胶产品，难溶于水难分解消化，现行常用的处理方法是火力燃烧，在解决固体废物污染的同时却造成了严重的空气污染。与此同时，建筑工程行业为了满足房屋建筑节能的要求，需要在建筑外墙墙体材料表面做保温隔热层，这些墙体保温材料仍然存在保温隔热效果不好、重量大、抗裂性能、抗冲击韧性、抗冻性能、抗渗性能以及防震减噪性能不好等问题。
技术实现思路
本专利技术的目的在于利用轮胎废料、提高保温砂浆的抗冲击性及抗裂性，提出一种利用废旧轮胎料制成的保温砂浆。技术方案为实现上述专利技术目的，本专利技术提供了以下技术方案：一种利用废旧轮胎料制成的保温砂浆，原料按重量份包括：镁铝水泥25-35份，建筑石灰10-15份，自来水20-30份，中砂5-10份，经粉碎清洗后粒径不超过50目的废旧轮胎料颗粒10-15份，水交联性聚乙烯3-5份，丙酮3-5份。本专利技术的有益作用在于：1.废旧轮胎料具有较好的隔热性能和耐久性，经改性处理后与传统的水泥砂浆很好地结合在一起。2.本文档来自技高网...

【技术保护点】
1.一种利用废旧轮胎料制成的保温砂浆，其特征在于，原料按重量份包括：镁铝水泥25‑35份，建筑石灰10‑15份，自来水20‑30份，中砂5‑10份，经粉碎清洗后粒径不超过50目的废旧轮胎料颗粒10‑15份，水交联性聚乙烯3‑5份，丙酮3‑5份。

【技术特征摘要】
1.一种利用废旧轮胎料制成的保温砂浆，其特征在于，原料按重量份包括：镁铝水泥25-35份，建筑石灰10-15份，自来水20...

【专利技术属性】
技术研发人员：梁秋云，
申请(专利权)人：梁秋云，
类型：发明
国别省市：广西,45