The invention discloses a waterproof and high temperature resistant building gypsum and a preparation method thereof, which relates to the technical field of building materials. The waterproof and high temperature resistant building gypsum comprises the following raw materials: waste gypsum module, desulfurization gypsum, crystallizer, sediment, lignosulfonate and naphthalene sulfonate formaldehyde polymer; the purity of the waste gypsum module is 88%-92% CaSO4.2H2O; the sand content in the sediment is 90-93%. The invention provides a waterproof and high temperature resistant building gypsum and a preparation method thereof. The preparation method is simple, and the obtained gypsum has good waterproof and high temperature resistance.
【技术实现步骤摘要】
一种防水耐高温建筑石膏及其制备方法
本专利技术涉及建筑材料
，尤其涉及一种防水耐高温建筑石膏及其制备方法。
技术介绍
石膏是单斜晶系矿物，其主要成分是硫酸钙(Ca2SO4)的水合物，它是一种用途广泛的工业材料和建筑材料，伴随着石膏制品业的发展，各种不同用途的石膏粉也相继得到推广，特别是在建材行业，随着人们生活水平的提高，对居住环境的品质要求越来越高，高端建筑日益不断增多，石膏可以用于水泥缓凝剂、石膏建筑制品和模具制作，已然成为建材市场的重要及紧俏的产品之一，所以如何进行石膏的循环再利用，已经成为人们研究的焦点之一。发生火灾时，市场上的墙体保温材料有些耐温性能较差，致使火灾蔓延，给人们的生命财产造成很大的危害，开发低碳与耐高温材料是科研工作者一直以来的追求，普通的石膏耐高温和防水的功能差。因此，极需要研发一种防水耐高温建筑石膏，并且能够利用废弃石膏作为原料，以废物循环利用来达到市场所需。
技术实现思路
针对上述存在的问题，本专利技术提供了一种防水耐高温建筑石膏及其制备方法，这种制备方法简单，所得石膏具有良好的防水、耐高温性能。本专利技术的技术方案为：一种防水耐高温...
【技术保护点】
1.一种防水耐高温建筑石膏，其特征在于，包括以下原料：废旧石膏模块、脱硫石膏、转晶剂、泥沙、木质素磺酸盐和萘磺酸盐甲醛聚合物；所述废旧石膏模块为纯度为88%～92%的CaSO4·2H2O；所述泥沙中沙的含量为90～93%。
【技术特征摘要】
1.一种防水耐高温建筑石膏，其特征在于，包括以下原料：废旧石膏模块、脱硫石膏、转晶剂、泥沙、木质素磺酸盐和萘磺酸盐甲醛聚合物；所述废旧石膏模块为纯度为88%～92%的CaSO4·2H2O；所述泥沙中沙的含量为90～93%。2.如权利要求1所述的一种防水耐高温建筑石膏，其特征在于，所述废旧石膏模块、脱硫石膏、转晶剂、泥沙、木质素磺酸盐和萘磺酸盐甲醛聚合物的重量比为：8:（1～2）:（0.5～0.8）:（1～3）：（0.002～0.003）:0.003。3.如权利要求2所述的一种防水耐高温建筑石膏，其特征在于，所述废旧石膏模块、脱硫石膏、转晶剂、泥沙、木质素磺酸盐和萘磺酸盐甲醛聚合物的重量比为：8:1.5:0.78:2：0.002:0.003。4.如权利要求1～3所述的一种防水耐高温建筑石膏，其特征在于，所述转晶剂为柠檬酸钠与硫酸锌的混合物，其中柠檬酸钠的质量百分比为0.025～...