The invention discloses an early strength and slightly expandable cement-based grouting material, whose raw materials are as follows: 200 400 portions of cement, 200 300 portions of coarse sand, 200 300 portions of medium sand, 50 150 portions of fine sand, 50 100 portions of auxiliary materials, 5 20 portions of water reducer, 5 30 portions of expansion agent, 1 3 portions of defoamer, 5 15 portions of rubber powder, appropriate amount of retarder, appropriate amount of early strength agent and 80 140 portions of water. Solve the early strength of grouting material; have super fluidity retention value, so that grouting material has good construction performance; the addition of dispersible rubber powder helps to improve the adhesion of grouting material and prevent cracking.
【技术实现步骤摘要】
一种早强微膨胀水泥基灌浆料
本专利技术涉及灌浆料领域，尤其涉及一种早强微膨胀水泥基灌浆料。
技术介绍
随着国内各种工程的加固、大型高层、超高层或地下建设工程的增大，对水泥基灌浆料的质量要求越高。水泥基灌浆料是一种由水泥、外加剂和矿物掺和料等原材料，经工厂化配制生产而成的具有合理级配的干混料。加水拌合均匀后具有可灌注的流动性、微膨胀、高的早期和后期强度、不泌水等性能。因其常温下具有高强度、自密实、无收缩等优异性能，在混凝土加固、修补、地脚螺栓锚固、设备基础建设、二次灌浆等方面具有广泛应用。近几年国内对灌浆料的研究也十分活跃，并取得很大突破。本专利技术采用普通硅酸盐及早强型硅酸盐水泥，通过多种新材料的选择及复配制备的水泥基灌浆料，具有超大保留流动度、早强、高强、抗渗等性能优点。
技术实现思路
本专利技术的目的是为了解决现有技术中存在的缺点，而提出的一种早强微膨胀水泥基灌浆料。为了实现上述目的，本专利技术采用了如下技术方案：一种早强微膨胀水泥基灌浆料，其原料按重量份如下：水泥200-400份，粗砂200-300份，中砂200-300份，细砂50-150份，辅料50-100份...
【技术保护点】
1.一种早强微膨胀水泥基灌浆料，其特征在于：其原料按重量份如下：水泥200‑400份，粗砂200‑300份，中砂200‑300份，细砂50‑150份，辅料50‑100份，减水剂5‑20份，膨胀剂5‑30份，消泡剂1‑3份，胶粉5‑15份，缓凝剂适量，早强剂适量，水80‑140份。
【技术特征摘要】
1.一种早强微膨胀水泥基灌浆料，其特征在于：其原料按重量份如下：水泥200-400份，粗砂200-300份，中砂200-300份，细砂50-150份，辅料50-100份，减水剂5-20份，膨胀剂5-30份，消泡剂1-3份，胶粉5-15份，缓凝剂适量，早强剂适量，水80-140份。2.根据权利要求1所述的一种早强微膨胀水泥基灌浆料，其特征在于：所述水泥为P.O52.5R水泥、硫铝酸盐水泥、P.O42.5水泥中的一种或多种。3.根据权利要求1所述的一种早强微膨胀水泥基灌浆料，其特征在于：所述粗砂、中砂和细砂的粒径均小于1mm，且其目数大小为20-40目、40-70目、70-140目，其...
【专利技术属性】
技术研发人员：郑建超，王英维，周普玉，
申请(专利权)人：山西佳维新材料股份有限公司，
类型：发明