A method for preparing lithium sodium cryolite from lithium fluoride includes the following steps: (1) adding lithium fluoride into inorganic acid solution and stirring to obtain acidified material; (2) adding aluminium salt and sodium salt to acidified material and stirring at 20-80 C to obtain mixture material; (3) filtering and separating filter residue from mixture material, washing filter residue, drying and removing water to obtain lithium sodium cryolite. The method of the invention uses common raw materials in the field of chemical industry, which is convenient to obtain, and has low requirements for experimental equipment, ordinary heating and stirring, simple operation, safety and reliability.
【技术实现步骤摘要】
一种用氟化锂制备锂钠冰晶石的方法
本专利技术属于材料
，特别涉及一种用氟化锂制备锂钠冰晶石的方法。
技术介绍
近年来，我国电解铝工业迅速发展，在铝电解质中除冰晶石(Na3AlF6)、氟化钠(NaF)、氟化钙(CaF2)等物相以外，锂钠冰晶石相(LiNa2AlF6、Li3Na3Al2F12)也是较为常见的，这两种物质一般均是在高温熔盐环境中形成。在目前的研究过程中，借助水溶液合成的方法去获得该物质的研究较少。
技术实现思路
本专利技术的目的是提供一种用氟化锂制备锂钠冰晶石的方法，通过酸溶氟化锂、加铝盐和钠盐、洗涤干燥等一系列步骤后制备得到不同的锂钠冰晶石组合；基于水溶液合成沉淀法，在较低温(20～100℃)的环境中得到目标产物。本专利技术的方法包括以下步骤：1、将氟化锂加入到无机酸液中，在30～80℃下搅拌反应20～60min，获得酸化物料；所述的无机酸液中的无机酸为HCl、H2SO4和/或HNO3，无机酸液的总浓度为0.8～1.2M；氟化锂和无机酸液的用量比例按固液比为20～40g/L；2、向酸化物料中加入铝盐和钠盐，在20～80℃下搅拌反应90～150min，...
【技术保护点】
1.一种用氟化锂制备锂钠冰晶石的方法，其特征在于包括以下步骤：(1)将氟化锂加入到无机酸液中，在30～80℃下搅拌反应20～60min，获得酸化物料；所述的无机酸液中的无机酸为HCl、H2SO4和/或HNO3，无机酸液的总浓度为0.8～1.2M；氟化锂和无机酸液的用量比例按固液比为20～40g/L；(2)向酸化物料中加入铝盐和钠盐，在20～80℃下搅拌反应90～150min，获得混合物料；其中铝盐的加入量按混合物料中Al和F摩尔比为1:(4～24)，钠盐的加入量按混合物料中钠与锂的摩尔比为1:1～1:3；(3)将混合物料过滤分离出滤渣，水洗滤渣至洗液为中性，将滤渣烘干去除水分，获得锂钠冰晶石。
【技术特征摘要】
1.一种用氟化锂制备锂钠冰晶石的方法，其特征在于包括以下步骤：(1)将氟化锂加入到无机酸液中，在30～80℃下搅拌反应20～60min，获得酸化物料；所述的无机酸液中的无机酸为HCl、H2SO4和/或HNO3，无机酸液的总浓度为0.8～1.2M；氟化锂和无机酸液的用量比例按固液比为20～40g/L；(2)向酸化物料中加入铝盐和钠盐，在20～80℃下搅拌反应90～150min，获得混合物料；其中铝盐的加入量按混合物料中Al和F摩尔比为1:(4～24)，钠盐的加入量按混...
【专利技术属性】
技术研发人员：陶文举，吴少华，王兆文，郑晏辰，陆羽，崔竞波，
申请(专利权)人：东北大学，
类型：发明
国别省市：辽宁,21
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。