The invention discloses a polypropylene composite material, which is prepared from polypropylene, elastomer, chopped glass fiber, additive liquid silicone rubber, initiator, scratch resistant agent, compatibilizer, antioxidant and other additives. The additive liquid silicone rubber and chopped glass fiber are mixed with polypropylene and melted to obtain a very low gloss on the surface of the product, both visually and tactilly. Can achieve good soft touch. Meanwhile, the tensile strength, bending modulus and notched impact strength of the polypropylene composite prepared by the invention can reach 23 MPa and 1600 MPa respectively, and the notched impact strength of the cantilever beam can reach 25 KJ/m.
【技术实现步骤摘要】
一种聚丙烯复合材料及其制备方法和应用
本专利技术属于高分子材料领域，具体涉及一种聚丙烯复合材料及其制备方法和应用。
技术介绍
近年来，为满足消费者追求舒适性、美观环保等需求，汽车内饰设计不仅要满足安全性能，还要求通过美学设计来让车内实现舒适温馨的感觉。聚丙烯来源丰富，价格低廉、易于加工，具有优异的机械性能和耐化学性能等优点，成为汽车内外饰中用量最大的聚合物，已经广泛的应用于仪表板、副仪表板、门板、立柱、门槛等产品中。传统的聚丙烯材质属于硬质塑料感，注塑成型的制件给人以硬邦邦的感觉，让消费者一种质感差、档次低的感觉，为了提高内饰件的舒适性档次，制造商往往表面会通过喷涂橡胶漆或者皮革包覆等来实现触感和回弹性，以此提升内饰的舒适性，但这种处理方法会存在成本增加、工序复杂、加工效率低、强度不符合要求等缺点，尤其是喷涂还会造成环境污染问题，因此也难以进行推广。
技术实现思路
基于此，本专利技术提供了一种聚丙烯复合材料，所述聚丙烯复合材料由聚丙烯、弹性体、短切剥离纤维、加成型液体硅橡胶、引发剂、耐刮擦剂、相容剂、抗氧剂、其他助剂制备而成，将加成型液体硅橡胶与聚丙烯熔融共混，赋予聚...
【技术保护点】
1.一种聚丙烯复合材料，其特征在于，由以下组分按照重量份数制备而成：聚丙烯 40~66份，弹性体 15~25份，短切玻璃纤维 15~30份，加成型液体硅橡胶 2~5 份，引发剂 0.5~1份，耐刮擦剂 1~2份，相容剂 2~5份，抗氧剂 0.2~0.4份，其他助剂 0~2.5份。
【技术特征摘要】
1.一种聚丙烯复合材料，其特征在于，由以下组分按照重量份数制备而成：聚丙烯40~66份，弹性体15~25份，短切玻璃纤维15~30份，加成型液体硅橡胶2~5份，引发剂0.5~1份，耐刮擦剂1~2份，相容剂2~5份，抗氧剂0.2~0.4份，其他助剂0~2.5份。2.如权利要求1所述的聚丙烯复合材料，其特征在于，所述聚丙烯为无规共聚聚丙烯、嵌段共聚聚丙烯中的一种或两种的组合，所述聚丙烯在230℃，2.16kg条件下的熔体流动速率为10~70g/10min。3.如权利要求1所述的聚丙烯复合材料，其特征在于，所述弹性体为乙烯-辛烯共聚物、乙烯-丁烯共聚物中的一种或两种的组合。4.如权利要求1所述的聚丙烯复合材料，其特征在于，所述短切玻璃纤维的长度为5~15mm，直径为4~25μm。5.如权利要求1所述的聚丙烯复合材料，其特征在于，所述的加成型液体硅橡胶的粘度为50~100Pa·S。6.如权利要求1所述的聚丙烯复合材料，其特征在于，所述耐刮擦剂为硅酮母粒、芥酸酰胺中的一种或两种的组合。7.如权利要求1所述的聚丙烯复合材料，其特征在于，所述抗氧剂包括主抗氧剂和辅助抗氧剂，所述主抗氧剂为四[β-(...
【专利技术属性】
技术研发人员：石阳阳，李飞，夏洋，周海，高勇，李荣群，闫溥，方宁，
申请(专利权)人：会通新材料股份有限公司，
类型：发明
国别省市：安徽,34