The invention belongs to the technical field of macromolecule, in particular to a polypropylene base material for gas permeation saturation foaming. The polypropylene base material is propylene, ethylene and butylene terpolymer: propylene, ethylene and butylene terpolymer has the following characteristics: melting point is 138-144 C, melting index MFR is 5.6-10.4 g/10 min, molecular weight distribution Mw/Mn is 3-6, and ethylene content is 0.5wt%-2.0wt%, butylene content is 4.0wt%-7.0wt%. Compared with the existing foamed polypropylene, the polymer provided by the invention has better mechanical properties, lower melting point, more suitable for gas permeation saturation foaming, higher foaming ratio, lower energy consumption in post-processing of high-rate foamed beads moulding, higher bonding strength and better toughness of foamed beads.
【技术实现步骤摘要】
一种用于气体渗透饱和法发泡的聚丙烯基料
本专利技术涉及高分子材料
，涉及一种用于气体渗透饱和法发泡的聚丙烯基料。
技术介绍
发泡聚丙烯材料EPP(ExpandedPolypropylene)，它是一种性能卓越的高结晶型聚合物/气体复合材料，以其独特而优越的性能成为目前增长最快的新型环保抗压缓冲隔热材料。EPP制品具有十分优异的抗震吸能性能、形变后回复率高、很好的耐热性(最高使用温度可达130℃)、耐化学品、耐油性和隔热性；同时，其质量轻，可大幅度减轻物品质量；另外，EPP还是一种环保材料，易于发生降解，且PP泡沫便于回收利用，其环境友好性优于其他发泡材料，因而被称为绿色泡沫。正是由于其表现出来的优异性能，使得EPP成为继聚苯乙烯(EPS)、聚氨酯(EPU)、聚乙烯(EPE)发泡材料之后更具应用价值和市场潜力的新型发泡材料。常规方法生产的PP是一种线型半结晶性聚合物，分子链很少支化，分子量分布相对较窄，这导致它的软化点和熔点很接近。在温度达到熔点之前，它基本不流动，当温度超过熔点后，熔体强度急剧下降，这种熔体很难包住气体；此外，聚丙烯从熔融态转变为结晶态会放出...
【技术保护点】
1.一种用于气体渗透饱和法发泡的聚丙烯基料，其特征在于：该聚丙烯基料为丙烯、乙烯和丁烯三元共聚物：其具有如下特征：熔点为138～146℃，熔融指数MFR为5.6～10.4g/10min，分子量分布Mw/Mn为3.0～6.0，且其中乙烯含量为0.5wt％～2.0wt％，丁烯含量为4.0wt％～7.0wt％。
【技术特征摘要】
1.一种用于气体渗透饱和法发泡的聚丙烯基料，其特征在于：该聚丙烯基料为丙烯、乙烯和丁烯三元共聚物：其具有如下特征：熔点为138～146℃，熔融指数MFR为5.6～10.4g/10min，分子量分布Mw/Mn为3.0～6.0，且其中乙烯含量为0.5wt％～2.0wt％，丁烯含量为4.0wt％～7.0wt％。2.根据权利要求1所述的聚丙烯基料，其特征在于：聚丙烯基料的熔点为139～142℃。3.根据权利要求1所述的聚丙烯基料，其特征在于：聚丙烯基料的熔融指数为6.8.～8.2g/10min。4.根据权利要求1所述的聚丙烯基料，其特征在于：聚丙烯基料的分子量分布Mw/Mn为3.5～6....
【专利技术属性】
技术研发人员：单国荣，周浩，唐学敏，黄惟毅，张锋，虞光财，翁向斌，时光，
申请(专利权)人：中国石油化工股份有限公司，中国石化上海石油化工股份有限公司，
类型：发明
国别省市：北京,11