本发明专利技术属于耐火材料技术领域，公开一种耐火聚烯烃橡胶及其制备方法，耐火聚烯烃橡胶由包括聚烯烃材料、陶瓷化粉、支撑填料、功能性添加剂的原料制得，该耐火聚烯烃橡胶通过改进的填料配方，使耐火聚烯烃在高温形成陶瓷体的过程中避免形成熔融收缩，以及发生线缆击穿，获得绝缘性能、力学性能以及耐火性能优异的陶瓷化聚烯烃材料。

Fire-resistant polyolefin rubber and its preparation method

The invention belongs to the technical field of refractory materials, and discloses a refractory polyolefin rubber and its preparation method. The refractory polyolefin rubber is prepared from raw materials including polyolefin materials, ceramic powder, supporting fillers and functional additives. The refractory polyolefin rubber avoids melting shrinkage in the process of forming ceramics at high temperature by improving the filler formula. Ceramic polyolefin materials with excellent insulation, mechanical properties and refractory properties were obtained by breakdown of cables.

【技术实现步骤摘要】
耐火聚烯烃橡胶及其制备方法
本专利技术涉及一种耐火材料，尤其是一种耐火聚烯烃橡胶及其制备方法。
技术介绍
耐火电缆具有规定的防火耐火性能，能够保证线路在火焰条件下继续稳定运行一段时间，使电力系统和信号控制系统在火焰条件下正常工作。目前，国内外防火耐火电缆主要有氧化镁矿物绝缘防火电缆和云母带绕包无机绝缘的防火耐火电缆。矿物绝缘防火电缆虽具有很好的防火耐火性能，但制造工艺复杂、生产成本高昂、施工难度很高。云母带绕包防火耐火电缆虽然工艺简单，但云母带高温燃烧后变脆，受到剧烈震动后易粉化脱落，耐火效果不佳。用陶瓷化硅橡胶制得耐火带施工简单、易操作，可批量化生产，但用陶瓷化硅橡胶制得的复合带成本较高，应用受到限制。可陶瓷化耐火硅橡胶电缆料需要凭借专用的橡胶挤出机挤出，并且还需要经过加热硫化工序进行硫化处理，因而工艺相对复杂，适用范围受到限制。低烟无卤阻燃聚烯烃电线电缆料是常用的一种绝缘性电缆料，但实际情况中，阻燃电缆在火灾中并不能有效的保护消防设备的线路安全，只能在火灾轰燃前，短时间阻碍火焰的快速传播，而轰燃发生后就必须依赖耐火电缆的作用。这导致了利用现有的生产设备生产可陶瓷化聚烯烃耐火电线电本文档来自技高网...

【技术保护点】
1.一种耐火聚烯烃橡胶，其特征在于，所述耐火聚烯烃橡胶由包括聚烯烃材料、陶瓷化粉、支撑填料、功能性添加剂的原料制得，所述支撑填料为亲水性气相法白炭黑、亲水性沉淀法白炭黑、亲水性高纯石英粉中的一种或几种，所述功能性添加剂为活性金属氧化物粉末。

【技术特征摘要】
1.一种耐火聚烯烃橡胶，其特征在于，所述耐火聚烯烃橡胶由包括聚烯烃材料、陶瓷化粉、支撑填料、功能性添加剂的原料制得，所述支撑填料为亲水性气相法白炭黑、亲水性沉淀法白炭黑、亲水性高纯石英粉中的一种或几种，所述功能性添加剂为活性金属氧化物粉末。2.如权利要求1所述的耐火聚烯烃橡胶，其特征在于，所述支撑填料的表面羟基数为2-10个/(nm2)。3.如权利要求1或2所述的耐火聚烯烃橡胶，其特征在于，以100重量份的聚烯烃材料计，所述支撑填料的用量为10-60重量份。4.如权利要求1所述的耐火聚烯烃橡胶，其特征在于，所述活性金属氧化物粉末包括氧化锌、氧化铝、氧化镁、氧化锆、氧化钛、氧化铝-氧化铁中的一种或几种。5.如权利要求1或3所述的耐火聚烯烃橡胶，其特征在于，所述功能性添加剂为活性氧化锌，比表面积大于30m2/g，或...