通信电缆用阻燃护套料及其制备方法技术

本发明专利技术公开了一种通信电缆用阻燃护套料及其制备方法，护套料包括以下组分：低密度聚乙烯树脂、环保增塑剂、萜烯树脂、卤化丁基橡胶、聚甲醛、丙二醇、活性纳米碳酸钙、电解锌酸浸渣、三聚氰胺氰尿酸盐、云母粉、重晶石粉、氢氧化铝阻燃剂、阻燃抑烟剂，本发明专利技术材料稳定性好，阻燃性能好，延展性高，生产的产品表面平整，柔韧性好。

Flame Retardant Sheath Material for Communication Cable and Its Preparation Method

The invention discloses a flame retardant sheath material for communication cable and its preparation method. The sheath material includes the following components: low density polyethylene resin, environmental plasticizer, terpene resin, halogenated butyl rubber, polyformaldehyde, propylene glycol, active nano-calcium carbonate, zinc acid leaching residue, melamine cyanurate, mica powder, barite powder, aluminium hydroxide flame retardant, flame retardant and smoke suppressant. The material of the invention has good stability, good flame retardant performance, high ductility, flat surface and good flexibility.

【技术实现步骤摘要】
通信电缆用阻燃护套料及其制备方法
本专利技术涉及一种护套料及其制备方法，特别涉及一种通信电缆用阻燃护套料及其制备方法。
技术介绍
电线电缆具有电力输送和信息输送的作用，在人们生活和生产中发挥着重要的作用，现有技术中，电缆行业通常使用PVC绝缘护套作为绝缘防护，而PVC绝缘护套采用PVC注塑料作为原料，但是由于PVC树脂的自身缺点，其阻燃性能较差，难以满足现有行业的需求。
技术实现思路
本专利技术的目的在于提供一种通信电缆用阻燃护套料及其制备方法。本专利技术采用的技术方案是：通信电缆用阻燃护套料，其特征在于：包括以下组分：低密度聚乙烯树脂85-105份、环保增塑剂15-35份、萜烯树脂25-35份、卤化丁基橡胶55-85份、聚甲醛10-20份、丙二醇2-6份、活性纳米碳酸钙2-10份、电解锌酸浸渣2-8份、三聚氰胺氰尿酸盐3-9份、云母粉12-22份、重晶石粉16-26份、氢氧化铝阻燃剂15-30份、阻燃抑烟剂25-35份。所述通信电缆用阻燃护套料的制备方法包括以下步骤：步骤1：将低密度聚乙烯树脂、环保增塑剂、萜烯树脂、卤化丁基橡胶、聚甲醛、丙二醇、活性纳米碳酸钙、电解锌酸浸渣、三聚氰胺氰本文档来自技高网...

【技术保护点】
1.通信电缆用阻燃护套料，其特征在于：包括以下重量份的组分：低密度聚乙烯树脂85‑105份、环保增塑剂15‑35份、萜烯树脂25‑35份、卤化丁基橡胶55‑85份、聚甲醛10‑20份、丙二醇2‑6份、活性纳米碳酸钙2‑10份、电解锌酸浸渣2‑8份、三聚氰胺氰尿酸盐3‑9份、云母粉12‑22份、重晶石粉16‑26份、氢氧化铝阻燃剂15‑30份、阻燃抑烟剂25‑35份。

【技术特征摘要】
1.通信电缆用阻燃护套料，其特征在于：包括以下重量份的组分：低密度聚乙烯树脂85-105份、环保增塑剂15-35份、萜烯树脂25-35份、卤化丁基橡胶55-85份、聚甲醛10-20份、丙二醇2-6份、活性纳米碳酸钙2-10份、电解锌酸浸渣2-8份、三聚氰胺氰尿酸盐3-9份、云母粉12-22份、重晶石粉16-26份、氢氧化铝阻燃剂15-30份、阻燃抑烟剂25-35份。2.根据权利要求1所述的通信电缆用阻燃护套料，其特征在于：所述通信电缆用阻燃护套料的...

【专利技术属性】
技术研发人员：何启新，
申请(专利权)人：海门市启新塑业有限公司，
类型：发明
国别省市：江苏,32