The invention discloses a light burning magnesium oxide retarder based on compound vitamins, which comprises the following components: 40-70 vitamin C, 10-20 vitamin B1, 10-20 vitamin B2 and 10-20 vitamin B6. The retarder is prepared by following steps: 1) crushing vitamin tablets into powder; 2) mixing the powder evenly at room temperature in proportion, namely, obtaining the required magnesium oxide retarder. The vitamin magnesia retarder provided by the invention provides a new idea for the preparation of cement-based material additives from the perspective of biological medicine, and the preparation process is simple, safe and non-toxic, and can significantly prolong the initial and final setting time.
【技术实现步骤摘要】
一种基于复合维生素的氧化镁缓凝剂、复合氧化镁及应用
本专利技术属于水泥基材料外加剂
，具体地说是一种基于复合型维生素的氧化镁缓凝剂、复合氧化镁及其应用。
技术介绍
轻烧氧化镁学名氧化镁，俗称菱苦土，是由菱镁矿在700～1000℃下煅烧得到，水化后体积会产生明显膨胀。在大体积水泥基材料中，水泥水化放热后期存在温度下降过程，产生收缩裂缝。掺入氧化镁能够有效补偿温降收缩，并使得整个体系产生微膨胀。轻烧氧化镁比表面积大、反应速度快，摆脱了重烧氧化镁活性低、反应慢的弊端，是补偿水泥收缩的理想材料。但与此同时，轻烧氧化镁的反应速度受温度影响较大。在夏季高温的环境中，氧化镁水化速度较快，水化产生氢氧化镁在大体积水泥基材料内部未产生温降收缩时就会带来巨大的膨胀，使得水泥基材料产生裂缝。现有技术中，通常使用铺设冷凝管，预冷骨料等手段进行降温，需要额外的成本。缓凝剂是一种降低水化速度和水化热、延长凝结时间的外加剂。使用缓凝剂来调控氧化镁的水化速度，既可以保证工程的施工质量，又节约了成本。因此从实际工程中考虑，在高温的环境中，需要通过缓凝剂去减缓氧化镁的水化速度。目前常用缓凝剂按...
【技术保护点】
1.一种基于复合维生素的氧化镁缓凝剂，其特征在于，所述缓凝剂包含以下重量份组分：40～70份维生素C、10～20份维生素B1、10～20份维生素B2以及10～20份维生素B6。
【技术特征摘要】
1.一种基于复合维生素的氧化镁缓凝剂，其特征在于，所述缓凝剂包含以下重量份组分：40～70份维生素C、10～20份维生素B1、10～20份维生素B2以及10～20份维生素B6。2.根据权利要求1所述的基于复合维生素的氧化镁缓凝剂，其特征在于，所述缓凝剂包含以下重量份组分：40～55份维生素C、15～20份维生素B1、15～20份维生素B2以及15～20份维生素B6。3.一种氧化镁复合物，其特征在于，所述氧化镁复合物的制备原料包含氧化镁以及如权利要求1或2所述的缓凝剂，所述缓凝剂与氧化镁的质量百分比为0.1～0.2％。4.根据权利要求3所述的氧化镁复合物，其特征在于，所述氧化镁复合物由以下方法制备：将氧化镁以及缓凝剂与适量的水混合，得氧化镁复合物；所述氧化镁为轻烧氧化镁。5.根据权利要求1或2任...
【专利技术属性】
技术研发人员：蒋林华，陈磊，杨国辉，靳卫准，徐鹏，陈晨，徐怡，
申请(专利权)人：河海大学，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。