发明专利技术公开了一种钛铝合金的制备方法，将钛制作为阳极，液态铝制作为阴极，在熔盐电解液中进行电解，制备得到钛铝合金。本发明专利技术钛铝合金的制备方法采用液态铝做阴极，在熔融状态下合金化，合金化的钛铝合金沉在坩埚底部，易于分离，该钛铝合金具有力学性能高、粗合金表面光滑、易于清洗，杂质含量少，便于下一步加工的优点。

A preparation method of titanium-aluminium alloy

The invention discloses a preparation method of titanium aluminium alloy. Titanium is made into an anode and liquid aluminium is made into a cathode, which is electrolyzed in molten salt electrolyte to prepare titanium aluminium alloy. The preparation method of the titanium aluminium alloy adopts liquid aluminium as cathode, and is alloyed in the melting state. The alloyed titanium aluminium alloy sinks at the bottom of the crucible and is easy to be separated. The titanium aluminium alloy has the advantages of high mechanical properties, smooth surface of the coarse alloy, easy cleaning, less impurity content and easy to be processed in the next step.

【技术实现步骤摘要】
一种钛铝合金的制备方法
本专利技术涉及一种钛铝合金的制备方法，属于合金加工

技术介绍
钛合金密度低，比强度高，耐腐蚀性、高温下抗蠕变性能和焊接性能良好，且生物相容性优异，被广泛用于航空航天、航海、化工、发电、汽车、体育休闲、医疗等领域。采用熔盐电解法制取钛铝合金已有下述几种：以废钛Ti6Al4V为可溶阳极，在碱金属氧化物盐系中进行电解制取(高玉璞、郭乃名，稀有金属，1997)，单用次方法生产的钛铝合金粉中除含铝量很低以外，最主要的缺点是：不同粒度含铝量不同，颗粒越小，韩亮亮越高，且随阳极回收率增加，含铝量增加，造成合金粉中含铝量不稳定，又由于铝细化晶粒，造成颗粒过细，含氧量不合格，不能满足制造结构件的要求。以废钛和铝的机械混合物作为可溶阳极，电解质组成为NaCl-KCl-MgCl2，其中含有1.0-1.5％的可溶钛盐，进行电解制取钛铝合金粉，采用此法生产处的钛铝合金粉，除含铝量可做得较高外，同样具有以上各项缺点。这是由于钛、铝虽是机械混合物作为阳极，但在电解温度下，实际上已完全合金化，生成了钛铝合金，所以不可避免要产生与使用钛合金完全相同的情况。以废钛、铝为可溶阳极，在Na本文档来自技高网...

【技术保护点】
1.一种钛铝合金的制备方法，其特征在于：将钛制作为阳极，液态铝制作为阴极，在熔盐电解液中进行电解，制备得到钛铝合金。

【技术特征摘要】
1.一种钛铝合金的制备方法，其特征在于：将钛制作为阳极，液态铝制作为阴极，在熔盐电解液中进行电解，制备得到钛铝合金。2.根据权利要求1所述的钛铝合金的制备方法，其特征在于：所述熔盐电解液由主体熔盐NaCl-KCl和可溶性钛盐组成。3.根据权利要求1所述的钛铝合金的制备方法，其特征在于...