A method for preparing fluorescent carbon quantum dots using eggs as precursors belongs to the field of preparing fluorescent carbon quantum dots. Natural biomass eggs were used as carbon source, and egg yolk and protein were separated by egg white separator. Water-soluble fluorescent carbon spots were obtained by microwave method, respectively. The invention has the advantages of easy access to raw materials, low cost, simple synthesis steps, fast acquisition, convenient operation, large-scale production, green environmental protection, and no need to add toxic chemical reagents. The results show that the obtained fluorescent carbon quantum dots have good water solubility and high fluorescence intensity, and have broad application prospects in cell imaging, biomarkers, catalytic engineering and biosensors, disease monitoring and prevention.
【技术实现步骤摘要】
一种以鸡蛋为前驱物微波法制备荧光碳量子点的方法
本专利技术属于荧光碳量子点制备领域，具体涉及一种以鸡蛋为前驱物微波法制备荧光碳量子点的方法。
技术介绍
碳元素构成了生命体的基本结构单元，例如氨基酸、多糖、蛋白质等，由此可以说明碳元素在生物体内有良好的生物相容性和生物安全性。2004年Xu等人，在分离和纯化单壁碳纳米管的过程中偶然发现了碳纳米粒子，并他们在后期的研究中不断探索纳米粒子的荧光性质试图去发展一种新兴的荧光纳米材料。2006年Sun等人，首次命名了这种荧光碳纳米粒子为碳量子点(CarbonDots，CDs)，并且提出了通过表面纯化的方法可以有效的增强荧光碳量子点的荧光发射强度。碳点，是指尺寸一般在10nm以下的碳纳米颗粒。因其表面带有丰富的功能团，如-OH，-COOH，C＝O等亲水性基团，而具有良好的水溶性。经过近十年对碳量子点的研究，碳量子点的制备方法一般总结为两种，分别为自上而下法，自下而上法。具体主要有燃烧/高温法、水热法、强酸氧化方法、微波法、溶液化学合成法、等离子体合成法等。然而这些方法通常都会以有机碳化合物作为碳源，合成条件苛刻，步骤繁琐，并且...
【技术保护点】
1.一种以鸡蛋为前驱物制备荧光碳量子点的方法，其特征在于：所述制备方法为微波法，具体制备步骤为：使用蛋白分离器来分别获得一定量的蛋白与蛋黄，分别搅拌均匀，放入一定功率的微波炉中加热一定时间，溶液分别由淡黄色、黄色颜色液体变至黑棕色固体，冷却至室温，然后将固体进行研磨，与去离子水进行混合搅拌，进行差速离心，取上层清液，使用孔径为0.22μm的滤膜抽滤，去上层清液透析，最后在‑20℃～‑60℃条件下，在冷冻干燥机中进行干燥2～3天，得到碳量子点粉末。
【技术特征摘要】
1.一种以鸡蛋为前驱物制备荧光碳量子点的方法，其特征在于：所述制备方法为微波法，具体制备步骤为：使用蛋白分离器来分别获得一定量的蛋白与蛋黄，分别搅拌均匀，放入一定功率的微波炉中加热一定时间，溶液分别由淡黄色、黄色颜色液体变至黑棕色固体，冷却至室温，然后将固体进行研磨，与去离子水进行混合搅拌，进行差速离心，取上层清液，使用孔径为0.22μm的滤膜抽滤，去上层清液透析，最后在-20℃～-60℃条件下，在冷冻干燥机中进行干燥...
【专利技术属性】
技术研发人员：李炳生，余立冬，魏新晶，贺金梅，李丽，陈洪宇，
申请(专利权)人：哈尔滨工业大学，
类型：发明
国别省市：黑龙江,23