The case discloses a nano silver graphene conductive adhesive and its preparation method. First, nano silver and graphene are prepared by chemical route, and then added into epoxy resin system to make conductive adhesive. In this case, a high performance conductive adhesive was prepared by attaching nano-silver with very small molecule to graphene sheets with super large specific surface area, which has good conductivity and high temperature resistance, and improved the adaptability of the material to large temperature and pressure differences. At the same time, the optimized preparation process can reproduce the preparation process of conductive adhesive. The preparation method is low cost, simple and convenient. Fast, suitable for large-scale production applications.
【技术实现步骤摘要】
一种纳米银石墨烯导电胶及其制备方法
本专利技术属于电子材料制备领域，具体涉及一种纳米银石墨烯导电胶及其制备方法。
技术介绍
电子元件不断向微型化的方向发展，器件集成度不断提高，这要求连接材料具有很高的线分辨率，传统的连接材料Pb/Sn焊料只能应用在0.65mm以下节距的连接,无法满足工艺需要；连接工艺中温度高于230℃产生的热应力也会损伤器件和基板；此外，Pb/Sn焊料中的铅为有毒物质。人们迫切需要新型无铅连接材料，导电胶作为一种Pb/Sn焊料的替代品应运而生。导电胶是一种同时具备导电性能和粘结性能的胶黏剂，它可以将多种导电材料连接在一起，使被连接材料间形成导电通路。一般而言，导电胶是通过将导电填料填充在有机聚合物基体中，从而使其具有与金属相近的导电性能。按导电胶中导电粒子的种类不同，可将导电胶分为银系导电胶、金系导电胶、铜系导电胶和炭系导电胶等,其中应用最广的是银系导电胶。银是优越的高导电导热金属，与金相比具有较大的价格优势，而目前的微米级银制备的体积电阻率只有10-4～10-3Ω·cm，无法满足导电性能需求，限制了在功率元件上的使用；纳米级银制备工艺复杂，并且...
【技术保护点】
1.一种纳米银石墨烯导电胶的制备方法，其特征在于，包括以下步骤：1)制备纳米银粉：将硝酸银溶于去离子水中，形成硝酸银稀溶液，加入聚乙烯吡咯烷酮和无水乙醇，搅拌30min后混合均匀，然后缓慢滴入质量分数为5％的水合肼溶液，用去离子水洗涤后在真空干燥至恒重，得到纳米级银粉；2)制备石墨烯：将石墨与过氧化钠混合加热，然后与碳酸氢钠在加热条件下反应2～3h；3)制备导电胶：将上述纳米银粉、石墨烯、环氧树脂、溶剂、增塑剂与固化剂放入游星式搅拌脱泡装置以1080r/min的速度高速搅拌30min，然后放入干燥箱中固化6h得到导电胶。
【技术特征摘要】
1.一种纳米银石墨烯导电胶的制备方法，其特征在于，包括以下步骤：1)制备纳米银粉：将硝酸银溶于去离子水中，形成硝酸银稀溶液，加入聚乙烯吡咯烷酮和无水乙醇，搅拌30min后混合均匀，然后缓慢滴入质量分数为5％的水合肼溶液，用去离子水洗涤后在真空干燥至恒重，得到纳米级银粉；2)制备石墨烯：将石墨与过氧化钠混合加热，然后与碳酸氢钠在加热条件下反应2～3h；3)制备导电胶：将上述纳米银粉、石墨烯、环氧树脂、溶剂、增塑剂与固化剂放入游星式搅拌脱泡装置以1080r/min的速度高速搅拌30min，然后放入干燥箱中固化6h得到导电胶。2.根据权利要求1所述的纳米银石墨烯导电胶的...
【专利技术属性】
技术研发人员：苏华，
申请(专利权)人：苏州团芯终端有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。