The invention relates to a building energy-saving pigment and a preparation method thereof, belonging to the preparation technology of building energy-saving pigment. The present invention reduces the carrier concentration in chromium oxide remarkably by doping proper amount of alumina, reduces the proportion of reflected infrared light, and reduces the infrared reflectivity. On the premise that chromium oxide and alumina form solid solution, the choice of sintering temperature can prevent the carrier concentration from increasing due to oxygen atom escaping, and then reduce the reflectivity. Compared with the existing technology, the invention has the advantages of multi-doping and simple process; while ensuring good solar radiation energy reflectivity, the green color system is relatively mild and harmless to human eyes, and the heavy metal doping is more environmentally friendly and cost-saving compared with the existing technology; and the relative density of other similar products is lower, which is more conducive to the lightening of pigments.
【技术实现步骤摘要】
一种建筑节能颜料及其制备方法
本专利技术涉及一种建筑节能颜料及其制备方法，属于建筑节能颜料的制备技术。
技术介绍
95％的太阳辐射处于可见光和近红外波段，建筑物吸收太阳辐射能量后提升了其表面温度，其温度的升高降低了人们的居住舒适度。人们往往采取空调制冷等方式降低建筑物温度，但是这种方式消耗了大量的能源。因此，增加建筑物的可见光和近红外区域反射率可以有效地降低建筑物的温度，从而缓解能源消耗的问题。涂层材料具有优异的性能，简单的工艺，便于施工和不受目标形状限制等优点，因此经常用来解决这方面的问题。氧化铬具有刚玉型结构，是一种稳定的两性氧化物，微溶于酸和碱，几乎不溶于水，常作为颜填料来制备涂料。其具有良好的化学稳定性(即优异的耐腐蚀性和温度稳定性)，易于着色，且具有和绿色植物相近的可见光-近红外光谱特性。在可见光波段表现为常见的绿色；而在可见光和红外光交界的红边处，其反射率的一阶导数十分巨大；在近红外波段，它的反射率也远高于可见光波段。由于它在红外波段的反射率较高，因此它被用于制备建筑节能颜料来反射太阳光的热量，达到降低建筑温度的目的。但是纯的氧化铬反射率还不够高，需要...
【技术保护点】
1.一种建筑节能颜料，其特征在于：为六角晶系的复合颜料，物相组成是氧化铝和氧化铬形成的刚玉型固溶体，表现为淡绿色，难溶于酸碱；其原料为氧化铝和氧化铬，按摩尔比1：0.12‑0.25在900‑1100℃的烧结温度下通过固相法制备。
【技术特征摘要】
1.一种建筑节能颜料，其特征在于：为六角晶系的复合颜料，物相组成是氧化铝和氧化铬形成的刚玉型固溶体，表现为淡绿色，难溶于酸碱；其原料为氧化铝和氧化铬，按摩尔比1：0.12-0.25在900-1100℃的烧结温度下通过固相法制备。2.如权利要求1所述建筑节能颜料的制备方法，包括下列步骤：步骤1、按氧化铬和氧化铝的摩尔比为1：0.12-0.25称取氧化铬和氧化铝，将其混合在一...
【专利技术属性】
技术研发人员：张林博，吴潘，孙贤，梁迪飞，谢建良，邓龙江，
申请(专利权)人：电子科技大学，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。