一种墙体表面用防水剂制造技术

本发明专利技术公开了一种墙体表面用防水剂，所述防水层的重量百分比的组分为水泥50%‑65%、乳液19%‑25%、分散剂1%‑2%、增塑剂5%‑7%、成膜助剂4%‑6%、填料5%‑8%、pH调节剂1%‑2%。在铺砌瓷砖层前，先在墙体的表面涂上该防水层，使墙体的表面形成防水层，使墙体具有防水的功能，使渗过瓷砖层的水汽只能依附在防水层上，防止水汽渗入墙体，避免墙体受潮发霉。

A Waterproof Agent for Wall Surface

The invention discloses a waterproof agent for wall surface, and the weight percentage of the waterproof layer is composed of cement 50%, 65%, emulsion 19%, 25%, dispersant 1%, 2%, plasticizer 5% 7%, film forming agent 4%, 6%, filler 5% 5%, and pH regulator. Before laying the ceramic tile layer, the waterproof layer is coated on the surface of the wall to form a waterproof layer on the surface of the wall, so that the wall has the waterproof function, so that the water vapor seeping through the ceramic tile layer can only adhere to the waterproof layer, so as to prevent the water vapor seeping into the wall and prevent the wall from damp and mildew.

【技术实现步骤摘要】
一种墙体表面用防水剂
本专利技术涉及墙体防水领域，尤其涉及一种墙体表面用防水剂。
技术介绍
建筑物外墙通常铺砌有瓷砖，用于墙体的防水，但建筑物外墙经常日晒雨淋，其表面的瓷砖层由于伸缩性较差，在铺砌时瓷砖每两两之间需要留有伸缩缝，以防止热胀冷缩导致的开裂或拱起，水汽长时间渗入，容易使墙体受潮发霉。
技术实现思路
本专利技术的目的在于克服现有技术的不足，提供一种墙体表面用防水剂，避免水汽使外墙受潮发霉。本专利技术解决其技术问题所采用的技术方案是：一种墙体表面用防水剂，所述防水层的重量百分比的组分为水泥50%-65%、乳液19%-25%、分散剂1%-2%、增塑剂5%-7%、成膜助剂4%-6%、填料5%-8%、pH调节剂1%-2%。进一步的，所述防水层的重量百分比的组分为水泥63%、乳液20%、分散剂1%、增塑剂5%、成膜助剂4%、填料6%、pH调节剂1%。进一步的，所述分散剂为聚丙烯或聚苯乙烯。进一步的，所述填料为钛白粉或滑石粉或碳酸钙。综上所述，本专利技术的有益效果是：在铺砌瓷砖层前，先在墙体的表面涂上该防水层，使墙体的表面形成防水层，使墙体具有防水的功能，使渗过瓷砖层的水汽只能依附在防水层上，防止水汽渗入墙体，避免墙体受潮发霉。具体实施方式实施例1本专利技术实施例1所描述的一种墙体表面用防水剂，所述防水层的重量百分比的组分为水泥63%、乳液20%、分散剂1%、增塑剂5%、成膜助剂4%、填料6%、pH调节剂1%。进一步的，所述分散剂为聚丙烯或聚苯乙烯。进一步的，所述填料为钛白粉或滑石粉或碳酸钙。以上所述，仅是本专利技术的较佳实施例而已，并非对本专利技术的结构作任何形式上的限制。凡是依据本专利技术的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本专利技术的技术方案的范围内。本文档来自技高网...

【技术保护点】
1.一种墙体表面用防水剂，其特征在于，所述防水层的重量百分比的组分为水泥50%‑65%、乳液19%‑25%、分散剂1%‑2%、增塑剂5%‑7%、成膜助剂4%‑6%、填料5%‑8%、pH调节剂1%‑2%。

【技术特征摘要】
1.一种墙体表面用防水剂，其特征在于，所述防水层的重量百分比的组分为水泥50%-65%、乳液19%-25%、分散剂1%-2%、增塑剂5%-7%、成膜助剂4%-6%、填料5%-8%、pH调节剂1%-2%。2.根据权利要求1所述的一种墙体表面用防水剂，其特征在于，所述防水层的重量百分比的组...

【专利技术属性】
技术研发人员：黄列旗，
申请(专利权)人：黄列旗，
类型：发明
国别省市：广东,44