The invention discloses an EVA sole, whose raw material composition includes: EVA: 80 120 copies; high pressure polyethylene: 25 40 copies; abrasive resistance: 8 14 copies; inorganic filling material: 15 25 copies; tackifier: 3 6 copies; white carbon black: 4 8 copies; stearic acid: 2 5 copies; rubber particles: 10 16 copies; and the above-mentioned copies are of quality. Preferably, the particle size of the inorganic filling material is less than 180 nm. Preferably, the rubber particle size is less than or equal to 260 nm. The beneficial effect of the invention is that the formula material of the invention is light, has good flexibility, has good shock resistance and cushioning performance, and improves the wear resistance of soles by improving the formula.
【技术实现步骤摘要】
一种EVA鞋底
本专利技术涉及一种EVA鞋底。
技术介绍
EVA鞋底是指使用EVA材料制成的鞋底，其鞋底回弹性和抗张力高，韧性高，具有良好的防震、缓冲性能，保温防寒及低温性能优异，可耐严寒，密闭泡孔，隔音效果也好，具有不吸水、防潮、耐水性能良好，耐酸、碱等化学品腐蚀，抗菌、无毒、无味、无污染的诸多优点。但EVA鞋底没有什么摩擦性，很容易滑倒。
技术实现思路
针对上述问题，本专利技术提供一种EVA鞋底，通过配方改进，提高鞋底的耐磨性能。为实现上述技术目的，达到上述技术效果，本专利技术通过以下技术方案实现：一种EVA鞋底，其原料组成包括：EVA：80-120份；高压聚乙烯：25-40份；耐磨剂：8-14份；无机填充材料：15-25份；增粘剂：3-6份；白炭黑：4-8份；硬脂酸：2-5份；橡胶颗粒：10-16份；上述份数均为质量份数。优选，所述无机填充材料粒径≤180nm。优选，所述橡胶颗粒粒径≤260nm。优选，所述EVA为110份，份数为质量份数。优选，所述高压聚乙烯为35份，份数为质量份数。优选，所述无机填充材料为22份，份数为质量份数。本专利技术的有益效果是：本专利技术的配方材料轻，柔软性好，具有良好的防震、缓冲性能，同时，通过配方改进，提高鞋底的耐磨性能。具体实施方式下面结合具体的实施例对本专利技术技术方案作进一步的详细描述，以使本领域的技术人员可以更好的理解本专利技术并能予以实施，但所举实施例不作为对本专利技术的限定。一种EVA鞋底，其原料组成包括：EVA：80-120份；高压聚乙烯：25-40份；耐磨剂：8-14份；无机填充材料：15-25份；增粘剂：...
【技术保护点】
1.一种EVA鞋底，其特征在于，其原料组成包括：EVA：80‑120份；高压聚乙烯：25‑40份；耐磨剂：8‑14份；无机填充材料：15‑25份；增粘剂：3‑6份；白炭黑：4‑8份；硬脂酸：2‑5份；橡胶颗粒：10‑16份；上述份数均为质量份数。
【技术特征摘要】
1.一种EVA鞋底，其特征在于，其原料组成包括：EVA：80-120份；高压聚乙烯：25-40份；耐磨剂：8-14份；无机填充材料：15-25份；增粘剂：3-6份；白炭黑：4-8份；硬脂酸：2-5份；橡胶颗粒：10-16份；上述份数均为质量份数。2.根据权利要求1所述的一种EVA鞋底，其特征在于，所述无机填充材料粒径≤180nm。3.根据权利...