The invention discloses an EVA foaming material, whose main raw materials include 16 copies of polyethylene octene co-elastomer, 2 copies of di-tert-butyl peroxyisopropylbenzene, 11 copies of TPR rubber particles and 5 copies of P P plastic particles, and its by-raw materials include 30 copies of filler, 1 copies of crosslinking agent, 2 copies of bridging agent, 0.5 copies of color masterbatch and 1.5 copies of foaming promoter. The EVA foaming material solves the problem that the EVA foaming material on the market can not further reduce the density under the condition of physical properties, improves the rebound effect of the EVA foaming material, and also enhances the elastic properties.
【技术实现步骤摘要】
一种EVA发泡材料及其加工工艺
本专利技术涉及EVA发泡材料加工
，具体为一种EVA发泡材料及其加工工艺。
技术介绍
目前，大多数的EVA发泡材料主要是聚苯乙烯(PS)、聚氯乙烯(PVC)、聚氨酯(PU)等，它给我们生活、生产带来极大方便的同时，不可避免的带来一些困扰，如难以降解而导致严重的城市“白色污染”，这些不可降解塑料随意丢弃时，破坏水源、土壤等生态；燃烧处理时，会产生有毒的“双酚”类物质，污染空气、危害人体健康。发达国家如美国、德国、日本等早就意识到EVA发泡材料废弃物对环境造成的危害，都先后制定了限用或禁用非降解EVA发泡材料的法规或增加附加税，这成为很多国家出口产品贸易壁垒的主要障碍之一。近年来，国内外对EVA发泡材料的研究和发展投入都比较多，使用者在对EVA发泡材料的使用上也提出了较高的要求，尤其对材质柔软程度、弹性以及耐弯折性的性能更加的看重，但是，现在市面上所使用的EVA发泡材料虽然已经在逐渐的靠近，还依然存在差距，在物理性能的条件下无法进一步的降低密度，反弹效果不佳，弹性性能也不高。
技术实现思路
(一)解决的技术问题针对现有技术的不足，本专...
【技术保护点】
1.一种EVA发泡材料，其特征在于：其主原料按重量份比包括：聚乙烯辛烯共弹性体16份、双叔丁基过氧异丙基苯2份、TPR橡胶粒11份和PP塑料粒子5份；其副原料按重量份比包括：填充剂30份、交联剂1份、架桥剂2份、色母粒0.5份和发泡促进剂1.5份。
【技术特征摘要】
1.一种EVA发泡材料，其特征在于：其主原料按重量份比包括：聚乙烯辛烯共弹性体16份、双叔丁基过氧异丙基苯2份、TPR橡胶粒11份和PP塑料粒子5份；其副原料按重量份比包括：填充剂30份、交联剂1份、架桥剂2份、色母粒0.5份和发泡促进剂1.5份。2.根据权利要求1所述的一种EVA发泡材料，其特征在于：所述聚乙烯辛烯共弹性体的牌号采用DF64056A，双叔丁基过氧异丙基苯的牌号采用25155-25-3，TPR橡胶粒的牌号采用7A60H，PP塑料粒子的牌号采用K8003，填充剂的牌号采用400目碳酸钙，架桥剂的牌号采用TAIC，色母粒的牌号采用黑色，发泡促进剂的牌号采用硬脂酸锌份。3.根据权利要求1-2任意一项所述的一种EVA发泡材料的加工工艺，其特征在于：具体包括以下步骤：步骤一、配料员根据主原料和副原料的具体重量进行配料；步骤二、将步骤一中配料好的主原料聚乙烯辛烯共弹性体16份、双叔丁基过氧异丙基苯2份、TPR橡胶粒11份和PP塑料粒子5份，以及副原料填充剂30份、交联剂1份、架桥剂2份...
【专利技术属性】
技术研发人员：邹晓明，
申请(专利权)人：无锡市铭明汽车内饰材料有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。