The invention discloses a tread base compound for skew heavy truck tire. According to the calculation of mass fraction, the tread base compound is composed of 100 natural rubber, 30-40 carbon black, 10-15 white carbon black, 1-3 vulcanizer, 0.8-2 accelerator, 0.1-0.4 plasticizer, 3-10 zinc oxide, 1-3 stearic acid, 2.5-4 antioxidant, 2-4 softening tackifier and 2-4 white carbon black surface. Activating agent 2-3 phr and anti-coke agent 0.1-0.3 phr were prepared. The tread base rubber for skew heavy truck tire prepared by the invention can reduce the tread temperature rise, reduce or eliminate the delamination failure of the shoulder of the tire, and improve the service life of the tire.
【技术实现步骤摘要】
一种斜交重卡轮胎用胎面基部胶料
本专利技术属于橡胶领域，尤其涉及一种斜交重卡轮胎用的一种胎面基部胶料。
技术介绍
斜交重卡轮胎主要在各类矿山场内倒运使用，路况恶劣，载荷较高，条件复杂。因此，重卡轮胎的胎面都做得比较厚，以增强抵抗路面对轮胎表面的破坏能力，胎体帘布层数都比较多，以增加轮胎胎体强度，提高负荷能力，防止爆胎。另一方面却导致行驶过程中轮胎在各种变形、外力作用下，轮胎胎面温度升高，散热慢，胶料性能下降，最终引发轮胎肩空脱层，失去使用价值。肩空已成为斜交重卡轮胎使用中的主要失效方式，造成极大的资源浪费，很多轮胎胎面花纹都还很深，却因为肩空脱层而无法继续使用，严重情况下会造成安全事故。因此现有的重卡轮胎的胶面还是不够理想，不能满足斜交重卡轮胎的需要。
技术实现思路
本专利技术的目的是针对现有技术中存在的不足，提供一种斜交重卡轮胎用的胎面基部胶料，降低轮胎胎面温升，减少或杜绝肩空脱层失效，提高轮胎使用寿命，从而克服现有技术的不足。本专利技术是这样实现的：本专利技术的一种斜交重卡轮胎用的胎面基部胶料,按照质量份计算（单位：kg），该胎面基部胶料是由100份天然胶、炭黑3...
【技术保护点】
1.一种斜交重卡轮胎用的胎面基部胶料,其特征在于：按照质量份计算，该胎面基部胶料是由100份天然胶、炭黑30～40份、白碳黑10～15份、硫化剂1～3份、促进剂0.8～2份、塑解剂0.1～0.4份、氧化锌3～10份、硬脂酸1～3份、防老剂2.5～4份、软化增粘剂2～4份、白碳黑表面活性剂2～3份、防焦剂0.1～0.3份制备而成。
【技术特征摘要】
1.一种斜交重卡轮胎用的胎面基部胶料,其特征在于：按照质量份计算，该胎面基部胶料是由100份天然胶、炭黑30～40份、白碳黑10～15份、硫化剂1～3份、促进剂0.8～2份、塑解剂0.1～0.4份、氧化锌3～10份、硬脂酸1～3份、防老剂2.5～4份、软化增粘剂2～4份、白碳黑表面活性剂2～3份、防焦剂0.1～0.3份制备而成。2.根据权利要求1所述的斜交重卡轮胎用的胎面基部胶料,其特征在于：所述炭黑为N330炭黑，所述N330炭黑为30～35份、白碳黑10～12份、所述促进剂为NS促进剂，所述NS促进剂为0.8～1....
【专利技术属性】
技术研发人员：吕强，王丽娥，苟登峰，邓旺，马玉宏，冯萍，
申请(专利权)人：贵州轮胎股份有限公司，
类型：发明
国别省市：贵州,52