The invention discloses a green composite foaming material and a preparation method, belonging to the field of natural polymer moulding and processing. The formulation of the green composite foaming material of the invention comprises cyanobacteria, 1_10 phr, cellulose 3_8 phr, pore-forming agent 30_180 phr and solvent 90_110 phr according to the weight fraction. In addition, the invention can also introduce water-soluble polymers and/or crosslinking agents, and further adjust the properties of green composite foaming materials. The green composite foaming material of the invention uses a large number of cyanobacteria in use, which makes the resource utilization of cyanobacteria feasible; the raw material is low in cost, easy to operate, easy to mass production, excellent mechanical properties, controllable pore structure size, and can be widely used in packaging liner, construction and other fields.
【技术实现步骤摘要】
一种绿色复合发泡材料及其制备方法
本专利技术涉及一种绿色复合发泡材料及其制备方法，属于天然高分子成型加工领域。
技术介绍
近年来，随着经济的快速发展，自然资源受到严重的破坏，众多工业废水和生活污水未经处理便排入湖泊中，致使湖泊水质变差，水体富营养化，进而导致了蓝藻水华的爆发。蓝藻水华的爆发严重影响了人们的正常生活，水质腥臭，造成了市民的用水困难，破坏了正常生活秩序。目前水华蓝藻的机械打捞仍是蓝藻处理的主要方式，但大量的打捞蓝藻若不能及时有效处置，随意堆放，不仅会因蓝藻的腐烂发臭造成二次污染，还会因氮、磷、藻毒素的地表途径或向下淋溶而给水体环境带来新的污染威胁。因此，探寻出一条蓝藻无害化处理与资源化利用途径对太湖污染治理意义重大。尽管近年来相关企业和研究部门对蓝藻的资源化利用的研究投入了大量的人力和物力，一系列蓝藻资源化利用技术，如发酵产沼气、发酵堆肥、提取藻蓝蛋白、以蓝藻为原材料制备塑料托盘、3D打印材料以及拖鞋等。但由于技术不成熟、生产成本以及市场化运营等问题，目前尚无市场化的商品面市。因此，提供一种新的、工业化应用可行性高的蓝藻资源化利用的处理方法是有迫切的市...
【技术保护点】
1.一种绿色复合发泡材料，其特征在于，所述材料的配方，按照重量份数配比，包括蓝藻1‑10份、纤维素3‑8份、成孔剂30‑180份、溶剂90‑110份。
【技术特征摘要】
1.一种绿色复合发泡材料，其特征在于，所述材料的配方，按照重量份数配比，包括蓝藻1-10份、纤维素3-8份、成孔剂30-180份、溶剂90-110份。2.根据权利要求1所述的材料，其特征在于，纤维素在溶剂中的固含量为3-6％。3.根据权利要求1所述的材料，其特征在于，所述材料的制备方法包括：(1)按照重量份数配比，将蓝藻和纤维素在溶剂中混合；(2)按照重量份数配比，加入成孔剂，混合得到混合浆液；(3)将混合浆液倒入模具，待定型，冷冻陈化成型得到混合体；(4)除去步骤(3)的混合体中多余的成孔剂、纤维素，即得绿色复合发泡材料。4.根据权利要求3所述的材料，其特征在于，所述材料的制备方法还可以包括：在步骤(2)中按照按照重量份数配比，加入解键剂1-5份。5.根据权利要求3或4所述的材料，其特征在于，所述材料的制备方法还可以包括：步...
【专利技术属性】
技术研发人员：王玮，张佰开，姜帅，华天予，吴泉钱，殷建钢，
申请(专利权)人：江南大学，无锡市城市环境科技有限公司，
类型：发明
国别省市：江苏,32