The invention discloses a self-repairing elemental sulfur terpene copolymer/epoxy resin composition and its preparation method, which first dissolves sulfur/terpene copolymer and epoxy resin in organic reagent, then adds reaction assistant, mixes evenly, removes organic solvent in vacuum, pours and forms, solidifies at 60-110 (?) C for 2-4 h, and then obtains crude product at 120-150 (?) C. The sulfur terpene copolymer/epoxy resin compositions with self-repairing properties were obtained by curing for 2-5 H. The preparation process of the elemental sulfur terpene copolymer/epoxy resin composition is simple and easy to operate, the reaction is efficient and stable, and the scratch can be thermally repaired at 40-80 C.
【技术实现步骤摘要】
一种具有自修复特性的单质硫-萜烯共聚物/环氧树脂组合物及其制备方法
本专利技术涉及材料领域，特别涉及一种具有自修复特性的单质硫-萜烯共聚物/环氧树脂组合物及其制备方法。
技术介绍
随着工业技术和社会生活的快速发展，高分子材料因其优异的力学性能、比重小以及易加工等优点，使得它们在现代生产生活中发挥越来越重要的作用。但材料在使用过程中必然会有损伤，若这些损伤未及时得到修复，材料的诸多性能都会退化直至不能使用，比如材料的强度和导热导电等高分子材料的优点就不能发挥出来，而且还会在使用中带来一定的安全隐患。受到仿生学的启示，利用高分子材料进行自修复研究就此诞生。现阶段，根据是否植入外部修复剂可以将自修复材料分为两大类：一类是外援型自修复体系，另一类是本征型自修复体系。本征型自修复体系是指利用自修复材料自身的化学结构特性，通过发生共价或非共价作用，在外界刺激下自行愈合损伤，部分或完全恢复受损材料的完整性和机械性能，从而达到自修复的目的。本征型自修复体系中的共价键作用主要包括动态共价化学、Diels-Alder反应、双硫键反应等。大多数的聚合物材料自修复效率和力学强度难以兼得，...
【技术保护点】
1.一种具有自修复特性的单质硫‑萜烯共聚物/环氧树脂组合物的制备方法，其特征在于：先将硫/萜烯共聚物、环氧树脂在有机试剂溶解；然后加入反应助剂，混合均匀，在真空下除有机溶剂，浇注成型，在60～110℃固化2～4h，得到粗产物；再将粗产物在120～150℃下固化2～5h，得到具有自修复特性的单质硫‑萜烯共聚物/环氧树脂组合物。
【技术特征摘要】
1.一种具有自修复特性的单质硫-萜烯共聚物/环氧树脂组合物的制备方法，其特征在于：先将硫/萜烯共聚物、环氧树脂在有机试剂溶解；然后加入反应助剂，混合均匀，在真空下除有机溶剂，浇注成型，在60～110℃固化2～4h，得到粗产物；再将粗产物在120～150℃下固化2～5h，得到具有自修复特性的单质硫-萜烯共聚物/环氧树脂组合物。2.根据权利要求1所述的具有自修复特性的单质硫-萜烯共聚物/环氧树脂组合物的制备方法，其特征在于：硫/萜烯共聚物的用量是环氧树脂质量的300％～500％。3.根据权利要求1所述的具有自修复特性的单质硫-萜烯共聚物/环氧树脂组合物的制备方法，其特征在于：反应助剂的用量是环氧树脂质量的0.5％～2％。4.根据权利要求1所述的具有自修复特性的单质硫-萜烯共聚物/环氧树脂组合物的制备方法，其特征在于：所述的环氧树脂为双酚A型环氧树脂或酚醛型...
【专利技术属性】
技术研发人员：许凯，孙龙凤，高树曦，桂雪峰，刘凌利，
申请(专利权)人：中科院广州化学有限公司，中国科学院大学，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。