The invention relates to the field of resources and environment, in particular to a method for recycling secondary aluminium ash. The method provided by the invention comprises the following steps: S1, sieving secondary aluminium ash after grinding, adding caustic soda (NaOH) solution and antiboiling agent after sieving, fully reacting at atmospheric pressure to produce without bubbles, collecting ammonia, hydrogen and methane; S2, diluting the filtrate after filtering at high temperature and high pressure, cooling the diluted filtrate to room temperature and precipitating aluminium hydroxide crystals; Aluminum hydroxide obtained after filtration is calcined to lose water to obtain alumina. The invention provides a method for efficiently recycling and utilizing secondary aluminium ash.
【技术实现步骤摘要】
一种二次铝灰资源化的方法
本专利技术涉及资源环境领域，具体涉及一种二次铝灰资源化的方法。
技术介绍
铝灰是电解铝、铸造铝和其他铝工业生产过程中必然产生的固体废渣，据测算，我国铝行业产生的二次铝灰达到350～400万吨/年。一次铝灰含有15～30％的金属铝，采用炒灰法回收其中大部分单质铝后，形成二次铝灰。二次铝灰仍含有5～8％的单质铝，无法采用炒灰法进一步提取出来。二次铝灰量非常大，导致堆积占用土地、严重污染环境等，然而二次铝灰中氧化铝含量占60～70％，有的甚至高达80～90％，比铝土矿中的氧化铝还要高，因此，作为垃圾处理甚为可惜。二次铝灰的高效回收利用已成为我国乃至世界性的难题。胡保国等(铝灰酸溶法制备聚合氯化铝，化工环保，33(4):325)以铝灰为原料采用酸溶法制备了聚合氯化铝(PAC)，并通过正交实验优化了PAC制备的最佳工艺参数，并考察了自制PAC对废水COD的去除效果。然而，铝灰中含有非常多的杂质，电解铝灰还含氟离子在3％以上，一步酸溶抽取PAC会吸附这些有毒杂质，无法直接用于净水的目的。专利技术专利(201510376294.2)公开了一种废铝灰制备...
【技术保护点】
1.一种二次铝灰资源化的方法，其特征在于，所述方法包括如下步骤：S1、将二次铝灰经研磨后过筛，筛后物和防沸剂加入NaOH溶液，在常压下进行充分反应至无气泡产生，收集氨气、氢气和甲烷；S2、在高温高压条件下，过滤后将所得滤液进行稀释，冷却稀释后的滤液至室温，析出氢氧化铝晶体；过滤后所得氢氧化铝煅烧失水得氧化铝；所述稀释为用水稀释至原体积的1.5～3.5倍。
【技术特征摘要】
1.一种二次铝灰资源化的方法，其特征在于，所述方法包括如下步骤：S1、将二次铝灰经研磨后过筛，筛后物和防沸剂加入NaOH溶液，在常压下进行充分反应至无气泡产生，收集氨气、氢气和甲烷；S2、在高温高压条件下，过滤后将所得滤液进行稀释，冷却稀释后的滤液至室温，析出氢氧化铝晶体；过滤后所得氢氧化铝煅烧失水得氧化铝；所述稀释为用水稀释至原体积的1.5～3.5倍。2.根据权利要求1所述的二次铝灰资源化的方法，其特征在于，步骤S1中，所述过筛为小于10目的筛网。3.根据权利要求1所述的二次铝灰资源化的方法，其特征在于，步骤S1中，所述加入防沸剂的质量百分比为二次铝灰的1～5％；所述防沸剂为活性炭和多孔合成酚醛树脂的混合物。4.根据权利要求3所述的二次铝灰资源化的方法，其特征在于，步骤S1中，活性炭和多孔合成酚醛树脂的...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。