The invention discloses a preparation method of aerogel hydrogel compound drug carrier, which relates to the field of drug carrier. Based on the problem of low aerogel mechanical property and limited load capacity of hydrogel, the invention comprises the following steps: active medicine is loaded in the pore of aerogel material, hydrophilic polymer and water form hydrogel skeleton, and gas loaded with active substances is coagulant. The adhesive material is evenly dispersed in the hydrogel, and the beneficial effect of the present invention is that the maximum drug load can be guaranteed, the best strength of the carrier in the transmission process can be guaranteed, and the intelligent and controllable drug release can also be realized.
【技术实现步骤摘要】
一种气凝胶-水凝胶复合药物载体的制备方法及制得的载体
本专利技术涉及药物载体领域，具体涉及一种气凝胶-水凝胶复合药物载体的制备方法及制得的载体。
技术介绍
气凝胶是一种具有高孔隙率，高表面积，低密度和纳米孔结构性质的材料。通过对气凝胶孔道表面进行化学改性，气凝胶可以具有非常丰富的表面功能。气凝胶材料可应用于建筑，工业，化妆品，生物化学等诸多领域。气凝胶具有非常高的孔隙率和纳米尺寸的孔隙，其可以在孔道内负载大量的活性药物，同时可以通过表面的化学基团实现其均匀、缓慢的释放。专利号为US20020094318A1的美国专利报道了利用气凝胶作为Methadone和MethadoneHydrochloride两种药物的载体，气凝胶载体可以有效的控制药物不被过量吸收，专利号为CN102961750A的中国专利首次报道了气凝胶微粉作为药物载体的应用先例。于其机械性能非常低，气凝胶通常作为复合材料或粉末应用。水凝胶是从一类可吸收并保留大量水的有合成或天然聚合物获得的三维网状结构物质。水凝胶具有低的界面张力、柔软、具有与生物组织结构相似的物理性质、透气性好，同时具有可控的药物释放表...
【技术保护点】
1.一种气凝胶‑水凝胶复合药物载体的制备方法，其特征在于：包括以下步骤：(1)将亲水性高分子化合物和水混合以形成高分子溶液；(2)将气凝胶与活性药物混合后，与步骤(1)中的高分子溶液混合；(3)将步骤(2)中的产物进行交联获得气凝胶‑水凝胶复合药物载体。
【技术特征摘要】
1.一种气凝胶-水凝胶复合药物载体的制备方法，其特征在于：包括以下步骤：(1)将亲水性高分子化合物和水混合以形成高分子溶液；(2)将气凝胶与活性药物混合后，与步骤(1)中的高分子溶液混合；(3)将步骤(2)中的产物进行交联获得气凝胶-水凝胶复合药物载体。2.根据权利要求1所述的气凝胶-水凝胶复合药物载体的制备方法，其特征在于：所述亲水性高分子化合物包括海藻酸钠、明胶、纤维素、壳聚糖、透明质酸、胶原蛋白、葡聚糖、聚乙烯醇、聚乙二醇、聚乙烯吡咯烷酮、聚氨酯、有机硅、聚甲基丙烯酸羟乙酯中一种或多种混合。3.根据权利要求1所述的气凝胶-水凝胶复合药物载体的制备方法，其特征在于：所述步骤(1)中亲水性高分子化合物的浓度为0.1％-20％。4.根据权利要求1所述的气凝胶-水凝胶复合药物载体的制备方法，其特征在于：所述气凝胶包括SiO2气凝胶、TiO2气凝胶、ZrO2气凝胶、Al2O3气凝胶、NiO气凝胶、ZnO气凝胶、碳气凝胶、碳纳米管气凝胶、石墨烯气凝胶中的一种或者多种。5.根据权利要...
【专利技术属性】
技术研发人员：张尚权，
申请(专利权)人：安徽科昂纳米科技有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。