The invention provides a durable flame-retardant fabric and its preparation method, which is interwoven by warp and weft yarns according to certain sinking and floating rules. The yarn is composed of 5%-10% polyimide grafted magnesium hydroxide, 30%-60% polyimide fiber, 30%-60% aramid fiber and 3%-5% ultra-fine stainless steel metal conductive fiber. By adding new flame retardants, the process flow was optimized, and the technical problems of flame retardant fibers in spinning and weaving process were solved. The permanent flame retardant effect of products was obvious, the fabric was strong, soft and comfortable, and the flame retardant effect was not affected after repeated washing.
【技术实现步骤摘要】
一种耐久阻燃面料及其制备方法
本专利技术涉及纺织
，具体地说，是一种耐久阻燃面料及其制备方法。
技术介绍
在火灾环境中，人们随时会面临燃烧的烈火、高温的液体、固体、气体等的侵害，通过接触、热辐射或热对流等途径到达人体，对人体造成危害，服装此时可以起到阻隔热能到达人体皮肤表面的作用。性能优异的阻燃防火服装，可以为人体提供有效地热防护，大大减小人体受伤害的几率和程度。对于消防人员和逃生者来说，防火服是一层关系到生命安全的重要皮肤，这层“皮肤”不仅要在短时间内隔绝人体与火源，还要在相对长的时间内代替人体皮肤接受火场的高温炙烤，因此防火服装对火场中消防人员的生命安全起到了至关重要的保护作用，也有利于为消防人员在救援时把握战机、高效的作业，防护服装将是防护人体免受伤害的最直接和最有效的手段。考虑到纺织品多与人体接触，因此其除了具备优良的阻燃性能外还需具有良好的舒适性：若织物的舒适性差，使用者就不愿选择该产品或者随意改变穿着方式以应付管理者，这样一旦发生火灾，就丧失了它的防护作用；特殊行业如消防员的灭火防护服在高温高湿的条件下使用，消防员没办法及时补充水分、缓解生理压力...
【技术保护点】
1.一种耐久阻燃面料，其特征在于，由经纱和纬纱按一定的沉浮规律上下交织而成，纱线由5％～10％聚酰亚胺接枝氢氧化镁，30％～60％聚酰亚胺纤维、30％～60％芳纶和3％～5％超细不锈钢金属导电纤维混纺而成。
【技术特征摘要】
1.一种耐久阻燃面料，其特征在于，由经纱和纬纱按一定的沉浮规律上下交织而成，纱线由5％～10％聚酰亚胺接枝氢氧化镁，30％～60％聚酰亚胺纤维、30％～60％芳纶和3％～5％超细不锈钢金属导电纤维混纺而成。2.根据权利要求1所述的耐久阻燃面料，其特征在于，所述聚酰亚胺接枝氢氧化镁的原料主要由氢氧化镁、4,4’-二氨基二苯醚、N,N-二甲基乙酰胺、均苯四甲酸二酐、异丙醇组成。3.根据权利要求2所述的耐久阻燃面料，其特征在于，纱线由5％聚酰亚胺接枝氢氧化镁，35％聚酰亚胺纤维、55％芳纶和5％超细不锈钢金属导电纤维混纺而成。4.一种耐久阻燃面料的制备方法，其特征在于，包括步骤:S100纺纱，将聚酰亚胺接枝氢氧化镁，聚酰亚胺纤维、芳纶纤维在开清工序混合，在混合纤维中添加聚醚酯抗静电剂，添加量为3～5kg/1000kg，再经梳理制成生条，超细不锈钢导电纤维经开清梳理制成生条，两者在并条工序并合、经粗纱、细纱工序纺成纱，在剑杆织机上织成阻燃面料；S200染色，将织造好的阻燃面料加入染色池，并在染料溶液中加入浓度8～10g/L的缓染剂、8～10g/L的冰醋酸，温度曲线100度开始上色，再降温，得到胚布；S300定形，...
【专利技术属性】
技术研发人员：董华，
申请(专利权)人：象山新光针织印染有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。