A preparation method for producing 3003 H14 aluminum alloy battery shell material includes the following steps: melting, sawing, soaking, milling, heating, hot rolling, cold rolling and annealing; in the melting and casting step, the chemical composition of the ingot after melting and casting is as follows: Si < 0.3%, Fe: 0.5 0.6%, Cu < 0.1%, Mn: 1.1 1.4%, Zn < 0.05%, Ti: 0.01 0.03%. The other impurities are single less than 0.02%, the other impurities are total less than 0.10%, and the rest are Al. The preparation method ensures that the mechanical properties of 3003 H14 aluminium alloy battery shell material are stable and qualified, the anisotropy is balanced during stamping, and the stamping performance is good.
【技术实现步骤摘要】
一种用于生产3003-H14铝合金电池壳材料的制备方法
本专利技术涉及铝合金制造领域，具体是涉及一种用于生产3003-H14铝合金电池壳材料的制备方法。
技术介绍
3003合金是Al-Mn系合金中应用较为广泛的合金之一，该系列合金产品具有强度适中、塑性好、冲压成型性好等特点。其H14状态的材料不仅具有较好的加工成形性，还具有适中的强度，作为新能源汽车电池壳材料生产，具有较高的应用价值，市场前景广阔。目前，3003-H14的传统工艺流程为：熔铸-锯切-均热-铣面-加热-热轧-冷轧-中间退火-冷轧-精整-包装。传统方式生产的3003-H14合金，无法保证铸锭和热轧坯料性能的均一，冲压过程中容易出现电池壳橘皮、制耳严重等现象。因此解决这一类的问题显得尤为重要，此技术是在制造铝合金电池壳材料工艺的设计和使用过程中予以考虑并解决的问题。
技术实现思路
鉴于上述现有技术的各种问题，本专利技术提供了一种用于生产3003-H14铝合金电池壳材料的制备方法，该生产制备方法保证了3003-H14铝合金板带材的力学性能稳定合格，冲压时各项异性均衡，具有良好的冲压性能。为了达到上述目的，本专...
【技术保护点】
1.一种用于生产3003‑H14铝合金电池壳材料的制备方法，其特征在于：所述制备方法包括如下步骤：熔铸、锯切、均热、铣面、加热、热轧、冷轧、退火；所述熔铸步骤中，熔铸后铸锭的化学成分的质量百分数为：Si≤0.3%、Fe：0.5‑0.6%、Cu≤0.1%、Mn：1.1‑1.4%、Zn≤0.05%、Ti：0.01‑0.03%、其它杂质单个≤0.02%、其它杂质合计≤0.10%，其余为Al。
【技术特征摘要】
1.一种用于生产3003-H14铝合金电池壳材料的制备方法，其特征在于：所述制备方法包括如下步骤：熔铸、锯切、均热、铣面、加热、热轧、冷轧、退火；所述熔铸步骤中，熔铸后铸锭的化学成分的质量百分数为：Si≤0.3%、Fe：0.5-0.6%、Cu≤0.1%、Mn：1.1-1.4%、Zn≤0.05%、Ti：0.01-0.03%、其它杂质单个≤0.02%、其它杂质合计≤0.10%，其余为Al。2.根据权利要求1所述的一种用于生产3003-H14铝合金电池壳材料的制备方法，其特征在于：所述熔铸步骤中，其中熔炼温度为740-760℃，精炼温度730-750℃，铸造温度685-695℃，铸造速度50-55mm/min。3.根据权利要求1所述的一种用于生产3003-H14铝合金电池壳材料的制备方法，其特征在于：所述均热步骤中，铸锭均热温度设定炉温5...
【专利技术属性】
技术研发人员：曹晓国，曹旷，李海峰，
申请(专利权)人：大力神铝业股份有限公司，
类型：发明
国别省市：江苏,32