The invention relates to a preparation method of water-borne dispersant, which dissolves styrene-maleic anhydride copolymer in inert solvent, adds monomethyl polyether and catalyst, heates to 60-110 degrees C, reacts for 2.5-6.0 hours, evaporates solvent, adds neutralizer, and mixes with viscosity reducer and wetting agent to prepare water-borne dispersant. Compared with the prior art, the dispersant prepared by the invention has good water solubility, good dispersibility and color development for pigments and fillers, and good viscosity reduction effect, and can form a color paste system with good performance, which can be widely used in the field of coatings and ink additives.
【技术实现步骤摘要】
一种水性分散剂的制备方法
本专利技术属于涂料、油墨助剂领域，尤其是涉及一种水性分散剂的制备方法。
技术介绍
目前，随着国家环保政策的日趋严格，涂料、油墨产品的水性化进程日益加紧，为了满足这类产品水性化进程，水性化助剂的研究成为热点。涂料和油墨这类产品对颜色的要求更是几近苛刻，所以颜料和填料的分散问题一直是技术关键所在，这类问题的解决很大程度上依赖高性能的分散剂，传统的小分子分散剂具有很多缺点，比如分散体系不稳定，储存时间短，容易形成团聚沉降。高分子类型的超分散剂很好的解决了这些弊端。对于苯乙烯-马来酸酐类体系的超分散剂，由于苯乙烯具有苯环结构，其对酞菁类颜料分散效果良好，马来酸酐作为分散无机填料的锚固基团，对无机颜料和体质颜料分散效果明显。但是苯乙烯-马来酸酐共聚物的水溶性并不好，这类高分子分散剂分散后的体系粘度较高，影响了后面色浆产品的流体性质；一般采用将马来酸用无机碱中和的方式来实现水性化，但是这样形成的分散体系，会对后面形成的涂层耐水性造成很大影响。
技术实现思路
本专利技术的目的就是为了克服上述现有技术存在的缺陷而提供一种成本较低且具备良好颜料、填料分散性的水...
【技术保护点】
1.一种水性分散剂的制备方法，其特征在于，将苯乙烯‑马来酸酐共聚物溶解于惰性溶剂中，加入单甲基聚醚和催化剂；加热至60～110℃，反应2.5～6.0小时，蒸去溶剂，加入中和剂中和到pH值为6.0～8.0，再与降粘剂、润湿剂混合搅匀，制备得到水性分散剂。
【技术特征摘要】
1.一种水性分散剂的制备方法，其特征在于，将苯乙烯-马来酸酐共聚物溶解于惰性溶剂中，加入单甲基聚醚和催化剂；加热至60～110℃，反应2.5～6.0小时，蒸去溶剂，加入中和剂中和到pH值为6.0～8.0，再与降粘剂、润湿剂混合搅匀，制备得到水性分散剂。2.根据权利要求1所述的一种水性分散剂的制备方法，其特征在于，所述苯乙烯-马来酸酐共聚物的重均分子量为2000～10000，分子量分布指数在1.0～2.0之间，共聚物的结构为无轨、嵌段或交替结构中的任一种。3.根据权利要求1所述的一种水性分散剂的制备方法，其特征在于，所述惰性溶剂为丙酮或乙酸乙酯等不与苯乙烯-马来酸酐共聚物反应的低沸点易挥发的溶剂(沸点低于100℃)。4.根据权利要求1所述的一种水性分散剂的制备方法，其特征在于，所述单甲基聚醚为丙二醇与乙二醇的嵌段共聚物，丙二醇与乙二醇的摩尔比为1:1～6，且由甲基在乙二醇一侧封端，数均分子量为500～3000。5.根据权利要求1所述的一种水性...
【专利技术属性】
技术研发人员：朱忠敏，叶小明，宗德超，
申请(专利权)人：东来涂料技术上海股份有限公司，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。