The invention discloses a cement-based self-leveling mortar, whose raw material composition is 32-37 Portland cement with strength grade 42.5, 32-37 Portland slag cement with strength grade 32.5, 68-72 portions of quartz sand, 25-28 portions of heavy calcium carbonate, 0.3-0.5 portions of polyvinylpyrrolidone (K30), 0.2-0.3 portions of cellulose ether, 0.4-0.6 portions of lithium sulfate, and 0.3 portions of calcium aluminate. 2-0.3 phr, Polycarboxylic Water Reducer 0.2-0.4 phr, latex powder 1.8-2.2 phr, retarder 0.15-0.25 phr, defoamer 0.25-0.35 phr. The self-leveling mortar has early strength, high abrasion resistance, good crack resistance, high fluidity and quick setting performance, fast construction, good quality and wide application.
【技术实现步骤摘要】
一种水泥基自流平砂浆及其制备方法
本专利技术属于建筑材料领域，具体涉及一种水泥基自流平砂浆及其制备方法。
技术介绍
地面用水泥基自流平砂浆是由水泥基凝胶材料、细骨料、填料及添加剂等组成，与水(或乳液)搅拌后具有流动性或稍加辅助性铺摊就能流动找平的地面用材料。水泥基自流平砂浆具有流平性能好、稳定性高、施工时间短等优势，可用于大面积仓库、工业厂房、生产车间、低下车库、商业卖场等开放空间及办公室的地面工程，其应用前景十分广阔。现有的水泥基自流平砂浆使用的水泥基凝胶材料通常为单独的强度等级为42.5及以上的普通硅酸盐水泥，或者将强度等级为42.5及以上的普通硅酸盐水泥与强度等级为42.5及以上的快硬硫铝酸盐水泥复合使用，以保证一定的硬度和抗压强度，但是，仍然存在早期强度不高、影响施工进程，易收缩开裂、产生质量缺陷，耐磨性不足等问题，使其应用领域受限。
技术实现思路
本专利技术的目的在于解决上述技术问题，提供一种早强、耐磨性高、抗裂性好的水泥基自流平砂浆，并且所述自流平砂浆还具有高流动性和速凝性能，其施工快速，质量优良，应用广泛。为了实现上述专利技术目的，本专利技术提供了以下技...
【技术保护点】
1.一种水泥基自流平砂浆，其特征在于所述自流平砂浆按重量份由以下原料制成：
【技术特征摘要】
1.一种水泥基自流平砂浆，其特征在于所述自流平砂浆按重量份由以下原料制成：组分重量份强度等级为42.5的普通硅酸盐水泥32～37份强度等级为32.5的矿渣硅酸盐水泥32～37份石英砂68～72份重质碳酸钙25～28份聚乙烯吡络烷酮(K30)0.3～0.5份纤维素醚0.2～0.3份硫酸锂0.4～0.6份铝酸钙0.2～0.3份聚羧酸类减水剂0.2～0.4份乳胶粉1.8～2.2份缓凝剂0.15～0.25份消泡剂0.25～0.35份2.根据权利要求1所述的水泥基自流平砂浆，其特征在于所述石英砂目数为120～170目。3.根据权利要求1所述的水泥基自流平砂浆，其特征在于所述纤维素醚为粘度6000～12000mPa·s的羟丙基甲基纤维素醚。4.根据权利要求1所述的水泥基自...