The invention relates to the technical field of power transmission, in particular to an aluminium-magnesium alloy wire used for high-voltage power cable bridge and its preparation method, which can improve the tensile strength and elongation, reduce the phenomenon of power cable breaking in contact with the bridge and reduce potential safety hazards; it is composed of the following raw materials: magnesium 3.8%6.2%; chromium 0.09%0.25%; iron 0.13%. % The preparation methods of 0.45%; copper 0.95%1.37%; titanium 0.06%0.12%; zinc 0.1%0.13%; rare earth element La 0.32%0.52%; rare earth element Ce 0.09%0.28%; Residual Aluminium include the following steps: (1) molten treatment of aluminium raw materials; (2) alloy addition; (3) magnesium addition; (4) moulding treatment.
【技术实现步骤摘要】
一种用于高压电力电缆桥架的铝镁合金线材及其制备方法
本专利技术涉及电力传输的
，特别是涉及一种用于高压电力电缆桥架的铝镁合金线材及其制备方法。
技术介绍
众所周知，高压电力电缆在架设过程中，需要使用电缆桥架作为支撑，以方便布线，高压电力电缆架设在桥架上的部分由于外界因素容易与桥架发生磨损，并且由于热胀冷缩的缘故，导致电缆容易发生断裂，形成一定的安全隐患。
技术实现思路
为解决上述技术问题，本专利技术提供一种可以提高抗拉强度以及延伸率，减少与桥架接触出的电力电缆断裂的现象，减少安全隐患的用于高压电力电缆桥架的铝镁合金线材及其制备方法。本专利技术的一种用于高压电力电缆桥架的铝镁合金线材，是由以下质量分数的原料组成的：镁3.8%-6.2%；铬0.09%-0.25%；铁0.13%-0.45%；铜0.95%-1.37%；钛0.06%-0.12%；锌0.1%-0.13%；稀土元素La0.32%-0.52%；稀土元素Ce0.09%-0.28%；铝余量。本专利技术的一种用于高压电力电缆桥架的铝镁合金线材，优选的，是由以下质量分数的原料组成的：镁4.7%-5.5%；铬0.15%-...
【技术保护点】
1.一种用于高压电力电缆桥架的铝镁合金线材，其特征在于，是由以下质量分数的原料组成的：镁 3.8%‑6.2%；铬 0.09%‑0.25%；铁 0.13%‑0.45%；铜 0.95%‑1.37%；钛 0.06%‑0.12%；锌 0.1%‑0.13%；稀土元素La 0.32%‑0.52%；稀土元素Ce 0.09%‑0.28%；铝 余量。
【技术特征摘要】
1.一种用于高压电力电缆桥架的铝镁合金线材，其特征在于，是由以下质量分数的原料组成的：镁3.8%-6.2%；铬0.09%-0.25%；铁0.13%-0.45%；铜0.95%-1.37%；钛0.06%-0.12%；锌0.1%-0.13%；稀土元素La0.32%-0.52%；稀土元素Ce0.09%-0.28%；铝余量。2.如权利要求1所述的一种用于高压电力电缆桥架的铝镁合金线材，其特征在于，优选的，是由以下质量分数的原料组成的：镁4.7%-5.5%；铬0.15%-0.19%；铁0.25%-0.32%；铜1.08%-1.23%；钛0.08%-0.10%；锌0.11%-0.12%；稀土元素La0.40%-0.46%；稀土元素Ce0.15%-0.20%；铝余量。3.一种用于高压电力电缆桥架的铝镁合金线材的制备方法，其特征在于，包括以下步骤：（1）铝原料熔融处理：将大部分铝在800-...
【专利技术属性】
技术研发人员：王素娟，
申请(专利权)人：东风线缆集团股份有限公司，
类型：发明
国别省市：河北,13