The utility model discloses an optimized lithium battery separator, which comprises a polyolefin microporous membrane and a heat-resistant coating. The two sides of the polyolefin microporous membrane are coated with a heat-resistant coating, in which the first coating is located at the lower end and the second coating is located at the upper end. The heat-resistant coating is an aluminium nitride coating. The thickness of the first coating and the second coating is 0.5 to 4.5 um, and the heat-resistant coating is described. The particle size D50 of the coatings is 1.0 2.0 um, and the BET is 3.5 5.0 M 2/g. The polyolefin microporous membrane has a single or multi-layer composite structure. The utility model coats the front and back sides of the polyolefin microporous membrane with aluminium nitride coating. When the diaphragm is heated, the thermal expansion coefficient of aluminium nitride is small, the thermal conductivity is good, and the mechanical strength is high. Compared with the pure polyolefin microporous membrane, the diaphragm has better shrinkage resistance and puncture strength.
【技术实现步骤摘要】
一种优化的锂电池隔膜
本技术涉及锂电池隔膜
，具体为一种优化的锂电池隔膜。
技术介绍
锂离子二次电池具有工作电压高，比容量、比能量高，无污染，无记忆效应，寿命长，自放电小，安全性好，循环寿命长和可快速充放电等优点，被广泛应用于数码电子、电器及电动汽车等产品领域，具有广阔的市场空间及良好的发展前景。目前国内隔膜大多数都是采用聚乙烯、聚丙烯及聚乙烯和聚丙烯结合的单层或多层的聚烯烃类隔膜。虽然聚烯烃隔膜在常温下可提供足够的机械强度和化学稳定性，但在高温条件下则表现出较大的热收缩，从而导致正负极接触并迅速积聚大量热。如PE隔膜，PE在120℃发生熔化阻塞聚合物中的微孔，当温度迅速上升，超过PP的熔融温度，隔膜熔融会造成大面积短路并引发急剧发热，引起电池燃烧或爆炸。PP也仅仅在165℃发生熔化阻塞聚合物中的微孔，同样引发安全隐患。另外市场上大多数采用氧化铝陶瓷涂覆隔膜，氧化铝涂覆隔膜具有一定的耐温性和高穿刺强度。但氧化铝型陶瓷隔膜具有硬度高易磨损生产设备、纯度低易造成锂电池电性能欠佳等缺点，不利于生产。
技术实现思路
本技术的目的在于提供一种优化的锂电池隔膜，其可以降低锂电池...
【技术保护点】
1.一种优化的锂电池隔膜，包括：聚烯烃微孔膜、耐热涂层，其特征在于：所述的聚烯烃微孔膜两侧涂有耐热涂层，其中位于下端面为第一涂层，位于上端面为第二涂层，所述的耐热涂层为氮化铝涂层，所述的第一涂层、第二涂层的厚度为0.5‑4.5μm。
【技术特征摘要】
1.一种优化的锂电池隔膜，包括：聚烯烃微孔膜、耐热涂层，其特征在于：所述的聚烯烃微孔膜两侧涂有耐热涂层，其中位于下端面为第一涂层，位于上端面为第二涂层，所述的耐热涂层为氮化铝涂层，所述的第一涂层、第二涂层的厚度为0.5-4.5μm。2.根...
【专利技术属性】
技术研发人员：刘淳，王翔，陈文健，
申请(专利权)人：江苏瑞发新材料科技有限公司，
类型：新型
国别省市：江苏,32