The invention discloses a new Wuxi self-polishing antifouling paint, which belongs to the field of coating technology and consists of raw materials with the following weight percentages: self-polishing resin 15%50%, hydrophobic resin 0.5%2%, auxiliary agent 4%7%, biocide 30%40%, powder filler 8%15%, colouring pigment 5%12%, solvent 10%. The total amount of raw materials is 100%. Compound resin cancels the use of cuprous oxide and reduces the content of copper in coatings; a small amount of strong hydrophobic resin is evenly embedded in coatings, which can improve the self-polishing performance of coatings and prevent microbial adhesion, at the same time, it can also control the slow release of antifouling agents and delay the service life of coatings.
【技术实现步骤摘要】
新型无锡自抛光型防污涂料
本专利技术涉及涂料
，尤其涉及一种新型无锡自抛光型防污涂料。
技术介绍
在海运过程中，海洋污着生物粘附生长在船舶水下的外壳部位，不但增加船体自身质量，而且显著加大了船底表面粗糙度，增大了船舶航行时的摩擦阻力，因此消耗了更多的船舶燃料，给船舶航行造成了严重的危害。为了减小这种危害，人们专利技术并使用了各种类型的防污涂料。20世纪50年代，人们发现防污漆中添加三丁基锡(TBT)后，能非常有效地抑制藤壶和海藻的生长，减小海洋生物附着带来的航行阻力，降低燃料成本，有效延长船舶的维修周期，于是有机锡防污漆得到了广泛的应用。但到了20世纪70年代后期，人们发现沿海海域逐渐出现了含毒三丁基锡的牡蛎和因此引发的物种变异现象，确认了防污漆中使用三丁基锡杀菌剂会造成生态上和经济上的海洋生物严重危害，人体健康也可能因消费受污染的海产品而受到损害。随着环境保护要求的日趋严格，不含有机锡、含有氧化亚铜的铜系防污剂对海洋生态环境的影响受到重视，比如中国专利CN102504697A、CN107141942A，都采用了氧化亚铜作为防污剂的组分。目前的这些无锡自抛光...
【技术保护点】
1.一种新型无锡自抛光型防污涂料，其特征在于，由下述重量百分比的原料组成：自抛光树脂： 15%‑50%疏水性树脂： 0.5%‑2%助剂： 4%‑7%生物杀灭剂： 30‑40%粉体填料： 8‑15%着色颜料： 5‑12%溶剂： 10‑15%；上述原料总计为100%。
【技术特征摘要】
1.一种新型无锡自抛光型防污涂料，其特征在于，由下述重量百分比的原料组成：自抛光树脂：15%-50%疏水性树脂：0.5%-2%助剂：4%-7%生物杀灭剂：30-40%粉体填料：8-15%着色颜料：5-12%溶剂：10-15%；上述原料总计为100%。2.根据权利要求1所述的新型无锡自抛光型防污涂料，其特征在于，所述自抛光树脂选自丙烯酸铜树脂或丙烯酸铜树脂与丙烯酸锌树脂、丙烯酸硅树脂的复配，其中所述自抛光树脂中铜的质量含量,以氧化亚铜计，占涂料的5%-20%。3.根据权利要求1所述的新型无锡自抛光型防污涂料，其特征在于，所述疏水性树脂选自改性硅树脂、有机氟改性聚氨酯、环氧树酯胶的一种或...
【专利技术属性】