类比高熵合金，本发明专利技术设计出ABO3钙钛矿高熵组分，制备出一种新型A位高熵钙钛矿氧化物(La0.2Li0.2Ba0.2Sr0.2Ca0.2)TiO3,为单一钙钛矿结构，不存在第二相，且其晶粒完整，元素分布均匀，可应用于介电材料等领域，可以通过组分微调同时定制多种物理性质，以满足实际需求；其巨大的成分探索空间，使其与传统钙钛矿氧化物相比，具有更多潜在的新性质和新应用。

A High Entropy Perovskite Oxide at A Site and Its Preparation Method

By analogy with high-entropy alloy, the ABO 3 Perovskite high-entropy component is designed, and a new A-site high-entropy perovskite oxide (La0.2Li0.2Ba0.2Sr0.2Ca0.2) titanium oxide (La0.2Sr0.2Ca0.2) is prepared. It has a single perovskite structure and no second phase, and has complete grain size and uniform element distribution. It can be used in dielectric materials and other fields. It can customize a variety of physical properties through fine-tuning of components at the same time to meet the actual needs. Compared with traditional perovskite oxides, it has more potential new properties and applications.

【技术实现步骤摘要】
一种A位高熵钙钛矿氧化物及其制备方法
本专利技术涉及钙钛矿氧化物
，具体是一种A位高熵钙钛矿氧化物及其制备方法。
技术介绍
钙钛矿是以俄罗斯矿物学家Perovski的名字命名的，最初单指钛酸钙矿物，后来把结构与之类似的晶体统称为钙钛矿物质。钙钛矿氧化物具有独特的晶体结构，尤其经改性后具有优异的性能，可被作为固体氧化物燃料电池的阴极材料、光催化剂、电介质材料、多铁性材料以及替代贵金属的氧化还原催化剂，是化学、物理和材料等领域研究的热点。钙钛矿结构可以使一些元素以非正常价态存在，具有非化学计量比的氧，或使活性金属以混合价态存在，使固体呈现某些特殊性质。掺杂多种阳离子可以同时定制ABO3钙钛矿氧化物的多种物理性质，以满足实际需求。钙钛矿结构中允许存在较大的容差因子，且A位处于八个八面体的空隙中，配位数为12，表明其具有一定的掺杂空间。高熵合金是由五种或五种以上元素按照等原子比或近等原子比的原则合金化，形成高熵固溶体的一类合金，由于各组元间较高的混合熵而倾向于形成固溶体，使得到的合金具有更优良的性能。
技术实现思路
类比高熵合金，本专利技术设计出ABO3钙钛矿高熵组分，制备出一种新型A位高本文档来自技高网...

【技术保护点】
1.一种A位高熵钙钛矿氧化物，其特征在于，其化学分子式为(La0.2Li0.2Ba0.2Sr0.2Ca0.2)TiO3。

【技术特征摘要】
1.一种A位高熵钙钛矿氧化物，其特征在于，其化学分子式为(La0.2Li0.2Ba0.2Sr0.2Ca0.2)TiO3。2.一种权利要求1所述的A位高熵钙钛矿氧化物的制备方法，其特征在于，包括以下步骤：步骤1：将原料La2O3、Li2O、BaO、SrO、CaO和TiO2按照分子式(La0.2Li0.2Ba0.2Sr0.2Ca0.2)TiO3的化学计量比进行精确称量，然后混合；步骤2：研磨混合好的原料；步骤3：烘干研磨后的粉料，并在1000～1200℃温度下预烧3～5h得到样品粉体；步骤4：再次研磨预烧好的样品粉体并烘干，烘干后加入粘结剂再次研磨并过筛；步骤5：称取一定量过筛后的粉体在3～5MPa的压力下压片，得到片状样品；步骤6：将压好的片状样品放入马弗炉中，温度升高至600℃排胶4～6h，然后将温度升高到1300～1500℃烧结8～12h，制得A位高熵钙钛矿氧化物。3.根据权利要求...

【专利技术属性】
技术研发人员：齐西伟，刘馨玥，杜强，闫金华，张晓燕，
申请(专利权)人：东北大学秦皇岛分校，
类型：发明
国别省市：河北,13